The Influence of the Accelerated Aging Conditions on the Properties of Polyolefin Geogrids Used for Landfill Slope Reinforcement

Abstract

Polyolefin geosynthetics are susceptible to oxidative degradation, which in turn leads to diminished mechanical properties in geotechnical constructions. When using these materials, it is extremely important to determine their durability over time in particularly aggressive conditions. In order to prolong the life of a geosynthetic material, antioxidants are added during the manufacturing process. The function of antioxidants is to prevent polymer oxidation reaction in time. As the antioxidant content is depleted, the polymer becomes less protected towards oxidative attacks. This article describes the aging process of uniaxial (high density polyethylene) HDPE geogrids under the influence of chemical and environmental factors. Evaluations of accelerated aging test of the uniaxial HDPE geogrids were incubated in simulated landfill conditions for a period of 12 months. Three temperatures (25 °C, 45 °C, and 75 °C) were selected for carrying out the aging experiments in aqueous solutions mimicking landfill conditions. The changes observed by differential scanning calorimetry (DSC), Fourier transform infrared spectroscopy (FTIR) and melt flow index (MFI) correlate with the mechanical properties of the aged geogrid. No significant changes in the FTIR and MFI were observed over the 12 months of accelerated aging tests at none of the three different temperatures. The oxidation induction time (OIT) test showed no antioxidant remaining in the geogrid following eight months of aging test at 75 °C. No significant changes in the influence of accelerated aging tests on the average relative elongation at 25 °C and 45 °C of the tested material were observed. Accelerated aging tests at 75 °C showed that the mean elongation of 12.12% for the sample not subjected to accelerated aging tests (new sample) increased to 19.32% (after 12 months of incubation).

Influence of Aging on the Physical Properties of Knitted Polymeric Materials

“…Due to aging, the physical-mechanical properties of these materials can be drastically affected when exposed to various influencing factors such as light, heat and water. Recently, researchers from various fields have made considerable efforts to investigate the extent of changes in polymeric materials due to certain exposures [ 1 , 2 , 3 , 4 , 5 , 6 , 7 , 8 , 9 , 10 ]. The efforts of scientists have led to the development of various test methods and instruments to accelerate material aging using fluorescent/UV light.…”

Evaluation of Interface Shear Strength Coefficient of Alternative Geogrid Made from Para Rubber Sheet

“…Geosynthetic material is used to provide one or more functions including reinforcement, separation, energy absorption, etc. A geogrid is one type of geosynthetic [ 1 ], which is used for the reinforcement function to increase soil strength. Normally, a geogrid is installed within the soil structure or between the soil layers.…”

Investigating the Effect of Photo-Oxidative Degradation on the Ageing Resistance of the Car Mudflaps Manufactured with Post-Production High-Density Polyethylene Wastes

“…The ageing process is determined by many factors that entail a whole set of changes in the strength and usage properties of plastic products [1][2][3][4]. These changes usually occur very slowly, with diffi culty to cath and the factors at work are diffi cult to measure.…”