The Influence of Galvanizing on the Surface Quality and Part Precision of S235J0 Alloy Machined by Turning

Abstract

This scientific paper aims to determine the optimal economic roughness of galvanized surfaces by studying the influence of turning surface roughness on the quality of galvanizing. The thickness of the zinc layer, its corrosion resistance, and the precision of the galvanized parts were also examined. S235J0 steel samples were processed using a turning operation to obtain different roughness values. Three galvanizing technologies, galvanic galvanizing, hot dip galvanizing, and hot dip galvanizing with centrifugation, were used in the experiments. The surface evolution from turning to zinc layer deposition was monitored, and parts were subjected to salt spray corrosion resistance testing. Statistical analysis confirmed the stability of the technologies used and the accuracy of the experimental data. Optimal roughness ranges for galvanizing were determined based on the quality of the surface before galvanizing and the galvanizing technology used. The findings show that avoiding small roughness values leads to savings in the machining phases. From the dimensional accuracy perspective, the parts have smaller dimensions after galvanizing, and the dimensional accuracy decreases. The study confirms that steel parts are protected from corrosion, and degradation of the zinc layer is more advanced in sections with less roughness. The optimal surface roughness values before galvanizing were determined to be Ra < 3.657 m in the case of HDG, Ra < 3.344 m in the case of HDG+C, and Ra > 2.928 μm in the case of ZP. The conclusions drawn from this study introduce new directions of research.

Characterization and Corrosion Behavior of Zinc Coatings for Two Anti-Corrosive Protections: A Detailed Study

“…Its multilayer coating provides high wear resistance, which is necessary for processing metal materials. The data in Table 2 are extracted from the authors' paper [13] and represent a summary of the evolution of surface roughness after different galvanizations. The study was oriented to determine the influences on the surface quality of the specimen after galvanization depending on the type of galvanization and the roughness of the initial substrate.…”