The influence of fiber addition and different fabrication conditions in manufacturing plasma treated polyethylene/carbon fiber composites

Abstract

The potential advantage of plasma treated polyethylene (PEP) in mechanical properties was studied in this research. Recycled carbon fiber (CF) was the filler used for this hand layup technique. During fabrication, 4–14 wt% CF was incorporated into PEP and the results showed the impact of both filler and plasma treatment in enhancing the mechanical strength of polymer composites. Tensile results improved from 17.51 to 22.51 MPa in the polyethylene (PE) matrix. Scanning electron microscope (SEM) results showed untreated PE composites with fiber and matrix breakages as also voids reducing the compatibility of the PE/CF phases. The maximum flexural property of 25.5 MPa was observed in 10 wt% CF/PE treated with plasma. This combination was tried with different fabrication conditions in a temperature range of 180–220°C and time duration of 20–30 min. It was clearly seen that CF/PE combinations at a temperature of 180°C and time duration of 20 min had maximum tensile and flexural strength. The optimization using Taguchi method proved the significance of CF content in enhancing the mechanical properties. It also observed better tensile strength, flexural strength properties with 10 wt% CF, 180°C temperature, 20 min time from the results. Surface images of this condition showed more dispersed CF in the PE than other combinations due to optimum temperature and time duration during fabrication.

Effect of hybridization on mechanical and water absorption properties of short palmyra palm leaf stalk/carbon fibers reinforced polyester composites

“…Natural fiber (NF) added composites have been growing in popularity due to the ever‐increasing demand for products with lower environmental and energy footprints. Industries use NFs in product development due to the high demand for eco‐friendly components 1,2 . Natural fibers are more desirable due to their lightweight, affordability, availability, minimum processing energy, and environmental friendliness 3,4 .…”