The Effect of La on the Surface Properties of Plasma Nitrided CoCrCuFeNi High-Entropy Alloys at 440 Degrees Celsius

Abstract

This paper investigates the effect of the element La on plasma nitriding of the CoCrCuFeNi high-entropy alloy (HEA) at 440 °C for 8, 16, and 24 h. The phase composition, morphology, and hardness distribution of the nitrided layer are characterized using XRD, optical microscopy, and a microhardness tester. Furthermore, the corrosion resistance is tested using an electrochemical workstation. The study evaluated the friction and wear performance using a testing machine and scanning electron microscope. The thickness of the effective hardening layer after 16 h of treatment with La was similar to that after 24 h of treatment without La. The addition of La significantly increased the growth rate constant of the effective hardening layer from 0.53 × 10−14 m2/s to 0.72 × 10−14 m2/s. In addition, an expanded FCC phase with greater interplanar spacing can be formed on the surface of the sample by introducing La into the plasma nitriding process. This indicates that the expanded FCC phase, with a higher concentration of interstitial nitrogen atoms, can effectively improve the corrosion resistance of the specimen surface. The corrosion rate of the specimen surface was reduced by 27.5% and the wear rate was reduced by 41.7% after 16 h of treatment with the addition of La compared to 24 h of nitriding without the addition of La. It has been shown that the addition of La to the plasma nitriding process results in a higher quality nitrided layer in a shorter time and also demonstrates that La has the potential to optimize the surface properties of plasma nitrided HEAs.