Synthesis, Structure, and Magnetism of CN3H6·VO(H2O)(HPO4)(H2PO4)·H2O, a New Guanidinium Vanadium(IV) Phosphate

Hydrothermal synthesis and characterization of a new 3D vanadium(III) phosphite (C4H8N2H4)0.5(C4H8N2H3)[V4(HPO3)7(H2O)3]1.5H2O

“…Hydrothermal synthesis has been successful for the preparation of microporous materials and other important solids. A variety of 1D chain [1][2][3][4], 2D layer [1,[5][6][7][8][9], and 3D open-framework structure [10][11][12][13][14][15][16][17][18][19][20][21][22][23] vanadium phosphates were prepared in the presence of organic amine, and alkali metal cation or metal complex as structure-directing agents. It is interesting that [HN(CH 2 CH 2 ) 3 3 ] 2À unit may lead to novel connectivity patterns compared to those observed in vanadium phosphates containing tetrahedral PO 4 units.…”

[VO(SeO3)(H2O)2]·0.5H2O

“…Atoms O1 and O3 complete the vanadium coordination sphere; both of these also link to Se. The bond valence sum (BVS) for V1, calculated by the Brown & Altermatt (1985) method, is 4.09 (expected value 4.00) assuming that V IV is present, which is supported by the pale-blue crystal colour of (I) (Bircsak et al, 1999).…”

Offene Gerüststrukturen von Übergangsmetallen

“…Diese Struktur findet sich nur bei wenigen Übergangsmetallen (V,59a Co,59b, c Cu59d und Nb59e). Ein wirklich tetraedrisch koordiniertes Übergangsmetall, das eine solche 1D‐Kette bildet, weist keine Bindungen außerhalb der Kette auf, bei höherer Koordination (5, 6) jedoch treten zusätzlich Bindungen zu endständigen Liganden oder Wassermolekülen auf 59a. Diese Art von zusätzlichen Bindungen scheint häufiger zu sein, wenn die Viererringe seitenverknüpft sind, also eine 1D‐Leiterstruktur bilden (Abbildung 5 c).…”