Synthesis and Ultrahigh Pressure Compression of High-Entropy Boride (Hf0.2Mo0.2Nb0.2Ta0.2Zr0.2)B2 to 220 GPa

Abstract

The high-entropy boride (Hf0.2, Mo0.2, Nb0.2, Ta0.2, Zr0.2)B2 material was synthesized under high-pressures and high-temperatures in a large-volume Paris-Edinburgh (PE) press from a ball-milled powder mix of HfO2, MoO3, Nb2O5, Ta2O5, ZrO2, carbon black, and boron carbide. The transformation process was monitored in situ by energy-dispersive x-ray diffraction with conversion starting at 1100 °C and completed by 2000 °C with the formation of a single hexagonal AlB2-type phase. The synthesized sample was recovered, powdered, and mixed with platinum pressure marker and studied under high pressure by angle-dispersive x-ray diffraction in a diamond anvil cell. The hexagonal AlB2-type phase of (Hf0.2, Mo0.2, Nb0.2, Ta0.2, Zr0.2)B2 was found to be stable up to the highest pressure of 220 GPa reached in this study (volume compression V/V0 = 0.70). The third order Birch-Murnaghan equation of state fit to the high-pressure data up to 220 GPa results in an ambient pressure unit cell volume V0=28.16±0.04 Å3, bulk modulusKo = 407 ± 6 GPa, pressure derivative of bulk-modulus K0′ = 2.73 ± 0.045 GPa. Our study indicates that this high-entropy boride (Hf0.2, Mo0.2, Nb0.2, Ta0.2, Zr0.2)B2 material is stable to ultrahigh pressures and temperatures and exhibit high bulk modulus similar to other incompressible transition metal borides like ReB2 and Os2B3.