Synthesis and Sintering Behavior of Ultrafine (<10 nm) Magnesium Aluminate Spinel Nanoparticles

Abstract

This article reports a comparative characterization of ultrafine MgAl2O4 spinel nanoparticles synthesized by polymeric precursor (Pechini) and coprecipitation methods. The nanoparticles were evaluated in terms of purity and surface cleanliness, size distribution, state of agglomeration, and sintering behavior. Powders synthesized by the Pechini technique were highly agglomerated and revealed a bimodal particle size distribution centered around 12 and 27 nm. Thermal analysis and infrared spectroscopy measurements indicated that carbon species remained on the surface of the powders only to be released when temperatures exceeded 1000°C. Isothermal sintering of such nanopowders at 1300°C showed a maximum relative density of only 54%. MgAl2O4 synthesized via coprecipitation created small nanoparticles, around 5–6 nm after calcination at 800°C, with significantly less agglomeration. Compared with the precursor‐derived powders, excellent sinterability of the coprecipitated powders was obtained under the same sintering conditions. Relative densities above 90% were obtained after only 10 min, which further increased to greater than 95% after 20 min with no sintering aids or dopants. The results highlight the importance of purity and processing control to exploit the beneficial high sinterability of nanoparticles.

Aldose to ketose interconversion: galactose and arabinose isomerization over heterogeneous catalysts

“…Magnesium aluminate (Mg-Al-O) catalysts were prepared using the polymeric precursor or Pechini method. 29 Predetermined amounts of magnesium nitrate (MgIJNO 3 ) 2 ·6H 2 O, 98%, Vekton) and aluminum nitrate (AlIJNO 3 ) 3 ·9H 2 O, 98%, Vekton) were mixed and stirred at room temperature in distilled water. Thereafter, appropriate amounts of citric acid (99%) and ethylene glycol (>99%) (Sigma Aldrich) were added to this solution at room temperature.…”

Grain growth resistant nanocrystalline zirconia by targeting zero grain boundary energies

“…We have synthesized nanoparticles by using a reverse strike co-precipitation method that allows nanoparticles with sizes ,10 nm. 39 Measuring the effect of La 31 on the GB energy of YSZ is also a significant challenge. This is because GB energies are typically very small thermodynamic quantities, and hence attempts to measure absolute values are often frustrated due to elevated noise to signal ratio.…”

Surface and grain boundary energies of tin dioxide at low and high temperatures and effects on densification behavior

“…The clusters of nanoparticles suggest agglomeration, which is expected when using the polymeric precursor method, as described elsewhere. 23 The microstructure implies a significant area of grain boundary existing in each sample after annealing.…”