Synthesis and Key Characteristics of Nanocrystalline AlCuNiFeCr High-entropy Alloy by Mechanical Alloying and Sintering

Abstract

The present study is primary addressed to structural evolution of multi-component AlCoNiFeCr highentropy alloy (HEA) from elemental materials to solid solution during mechanical alloying (MA), and further, to equilibrium phases during subsequent thermal annealing and pressure sintering. It was justified experimentally that MA of Al-Cu-Ni-Fe-Cr powder mixture during 5 hours resulted in a single-phase nanocrystalline HEA with a structure of ВCC solid solution. During thermal annealing recovery and recrystallization of the BCC solid solution take place at temperatures ranging from 130 to 500 °C, and phase transformation, and grain growth of equilibrium phases occur at higher temperatures. The phase composition transforms to BCC and FCC solid solutions when the MA powder was annealed at 600 °C for 1 h. The BCC and FCC solid solution structure can be maintained even after the alloy was annealed at 1000 °C. The alloy powder was consolidated by pressure sintering at 800 °C with 5 GPa pressure for half an hour. The sintered samples exhibit 9.2±0.3 GPa in Vickers hardness.