Synthesis and Formation Mechanism of Textured MOF-5

Abstract

Textured and house-of-card structures develop on the surfaces of cubic MOF-5 crystals. The formation mechanism of these novel constructions are investigated based on characterisation of the intermediate specimens with different reaction time intervals using scanning and transmission electron microscopies. It is found that the growth of MOF-5 cubic crystals does not follow the classical route. MOF-5 nanocrystallites initially aggregate to form large polycrystalline cubes, followed by surface rearrangement of the nanocrystallites into a textured structure consisting of nanowires lying along the [100], [010], [110] and [110] zone axes, if the face of the cube is defined to be (001). Further crystal growth leads to a house-of-cards structure constructed by interpenetrated nanoplates with their shortest axis parallel to [110] and [110] axes. Evidence of a reversed crystal growth process is also observed. MOF-5 cubes with a single crystal-like appearance are achieved with extended reaction times despite their hidden three tier structure containing varying porosities hidden underneath.

A novel Ag/Ag3PO4‐IRMOF‐1 nanocomposite for antibacterial application in the dark and under visible light irradiation

“…The XRD pattern of IRMOF‐1 is in good consistency to previous reports . Also sharpness and high intensity of the peaks indicate high crystallinity of the materials …”

Electrodeposited metal-organic framework films as self-assembled hierarchically superstructured supports for stable omniphobic surface coatings

“…Greer et al . 62 concluded that the crystallisation proceeds via a reversed crystal growth route in which oriented aggregation of initially formed nanocrystallites is promoted by DBA also acting as surface ligand and spacer. In later stages, recrystallization occurs from the surface to the core.…”

Reversed Crystal Growth of Calcite in Naturally Occurring Travertine Crust

“…Instead, they underwent aggregation to form polycrystalline particles with a rhombohedral appearance (Figure 7d). Despite the short history of this reversed crystal growth route it has been used to explain the formation of many hollow and core-shell crystals in several inorganic systems including zeolites [48,74,75], perovskites [76], metal oxides [26,77], plus more recently organic resorcinarene hexamer [78], alloy nanoparticles [79] and metal organic frameworks [80,81]. There is a need for further extensive studies on the complex interactions between organic structure directing agents and metal cations to establish the role EPS plays in biomineralisation.…”