Synthesis and Dual-Mode Electrochromism of Anisotropic Monoclinic Nb₁₂O₂₉Colloidal Nanoplatelets

Abstract

Transition metal oxide nanocrystals with dual-mode electrochromism hold promise for smart windows enabling spectrally selective solar modulation. We have developed the colloidal synthesis of anisotropic monoclinic Nb12O29 nanoplatelets (NPLs) to investigate the dual-mode electrochromism of niobium oxide nanocrystals. The precursor for synthesizing NPLs was prepared by mixing NbCl5 and oleic acid to form a complex that was subsequently heated to form an oxide-like structure capped by oleic acid, denoted as niobium oxo cluster. By initiating the synthesis using niobium oxo clusters, preferred growth of NPLs over other polymorphs was observed. The structure of the synthesized NPLs was examined by X-ray diffraction in conjunction with simulations, revealing that the NPLs are monolayer monoclinic Nb12O29, thin in the [100] direction and extended along the b and c directions. Besides having monolayer thickness, NPLs show decreased intensity of Raman signal from Nb-O bonds with higher bond order when compared to bulk monoclinic Nb12O29, as interpreted by calculations. Progressive electrochemical reduction of NPL films led to absorbance in the near-infrared region (stage 1) followed by absorbance in both the visible and near-infrared regions (stage 2), thus exhibiting dual-mode electrochromism. The mechanisms underlying these two processes were distinguished electrochemically by cyclic voltammetry to determine the extent to which ion intercalation limits the kinetics, and by verifying the presence of localized electrons following ion intercalation using X-ray photoelectron spectroscopy. Both results support that the near-infrared absorption results from capacitive charging and the onset of visible absorption in the second stage is caused by ion intercalation. File list (2) download file view on ChemRxiv Maintext-04-09-2020.pdf (5.47 MiB) download file view on ChemRxiv SuppResults-04-09-2020.pdf (7.23 MiB)

Thymoquinone loading into hydroxyapatite/alginate scaffolds accelerated the osteogenic differentiation of the mesenchymal stem cells

“…The peak at 1615 cm −1 was assigned to the amino acids tyrosine, tryptophan and adenine and the peaks between 1640 and 1680 cm −1 were for Amide Ι [ 32 ], which indicated the presence of protein such as collagen that produced by the cells in the cultures. Also, the vibration at 1721 cm −1 [ 36 ], 1802 cm −1 , and 1869 cm −1 [ 37 ] represented CO binding. Alginate and proteins are CO-rich components; and therefore, these peaks may indicate the presence of protein or alginate that we used it as drug carrier in the scaffold.…”

Formation and growth mechanism for niobium oxide nanoparticles: atomistic insight from in situ X-ray total scattering

“…photodetection 11 and in recent years, the potential of amorphous and nanostructured Nb2O5 for electrochromic windows has been investigated. [12][13][14] The versatility of applications of niobium-based oxides arises from their rich structural chemistry. 9,15 The building block of niobium pentoxide Nb2O5 is the [NbO6] octahedra which occur in the oxide structures as corner-sharing or edge-sharing, i.e.…”

“…photodetection 11 and in recent years, the potential of amorphous and nanostructured Nb 2 O 5 for electrochromic windows has been investigated. 12–14 …”

Tunable Intracrystal Cavity in Tungsten Bronze‐Like Bimetallic Oxides for Electrochromic Energy Storage

“…That is to say, the obvious coloration within the near-infrared region in the first stage is mainly controlled by Li + adsorption on the surface of the Nb 18 W 16 O 93 nanomaterial, while a large number of lithium ions are embedded in five-, four-and three-membered rings of the Nb 18 W 16 O 93 nanomaterial during the second stage, resulting in significant optical density change in the visible region which is consistent with previous work. [39,40] Both electrochemical and electrochromic performance depend on the phenomena of electron transport and ionic intercalation-deintercalation. Here, we simulated the Li + free intracrystal cavity for the monoclinic WO 3 , orthorhombic Nb 18 W 16 O 93 , and orthorhombic Nb 2 O 5 crystal structures (see Figure 4a-c, 0.76 Å was used as probe radius).…”