Synthesis and Characterization of YCr_xAl_1-xO₃ Particles by a Reverse Micelle Processing

Abstract

YCrxAl1-xO3 nanoparticles were synthesized by a reverse micelle processing for inorganic pigment. Y(NO3)2·6H2O, Cr (NO3)2·6H2O and Al (NO3)3·9H2O are used for precursors in order to synthesis YCrxAl1-xO3 nanoparticles. The aqueous solution consists of mixing the molar ratio of Y/Cr/Al at 1:x:1-x and heat treated at 900~1300°C for 2h. The average size and distribution of synthesized YCrxAl1-xO3 powders was in the range of 10-20nm and narrow, respectively. The average size of the synthesized YCrxAl1-xO3 powders increased with increasing water to surfactant molar ratio and heating temperature. The crystallinity of synthesized YCrxAl1-xO3 powder increased with increasing heating temperature. The synthesized YCrxAl1-xO3 powders were characterized by X-ray diffraction analysis (XRD), field emission scanning electron microscopy (FE-SEM) and color spectrophotometer. The properties of the synthesized powders were affected by such variables as molar ratio, heating temperature etc.