Synthesis And Characterization Of Highly Crystalline Polyaniline Film Promising For Humid Sensor

Photocatalytic activity of nanopolyaniline (NPA) on phenol degradation

“…The absorption peaks observed at 328 and 631 nm are due to π-π* transition of benzenoid rings and absorption of the quinoid rings, respectively (Shukla et al, 2010) confirm the NPA emeraldine (aniline hydrochloride). Using the absorption edge wavelength as 631 the band gap energy of NPA was obtained as 1.96 eV which falls well within the visible region of electromagnetic radiation.…”

“…The observed most intense diffraction peak at 2θ = 21.254° are due to planes of benzinoid and quinoid rings. Shukla et al (2010) has reported a profile similar to that of NPA in the same synthetic routes. Crystallite size (D) of NPA calculated from Debye Scherer formula, described previously was 37 nm.…”

“…The NPA was synthesized by chemical oxidative polymerization method (Gospodinova and Terlemezyan, 1998;Shukla et al, 2010;Hirotsugu and Hiromasa, 2011;Srinivas et al, 2012). Typically, 2M aniline (C6H5NH2) and 2M ammoniumpersulphate [(NH4)2S2O8], each prepared in 1 MHCl solution, were mixed in a beaker and by magnetically stirred for 1 h and kept at room temperature for 12 h. The polymer thus formed was filtered out, washed with de-ionized water, and dried at 60°C in oven for 30 min.…”

Synthesis of Polyaniline Based Nanocomposite Graphite Paste Electrode Modified with and Without Rice Husk for Sensor Application: A Comparative Study

“…The last items (alkali and carbon dioxide) are electroinactive; subsequently, if an oxidation current is seen amid the enzymatic response, the middle item should be electrolyzed. In our past review [24,26], one of the last anode response results of urea amid electrolysis has as of now been affirmed to nitrogen. Further, it can be accepted that carbamic corrosive experiences three electrons oxidation to frame nitrogen and carbon dioxide.…”

Fabrication of Polymer Based Schottky Diode Using Pani/Ag Nano Composite

“…After 30min opaque blue solution was obtained and at the end of the reaction (after 45 min), the dark green color solution was yielded. The solution was filtered and dried and at the end dark green particles (polyaniline) were obtained [15].…”