Abstract:Cu-14Fe-0.05C alloy was prepared by using the vacuum melting process and then multipass drawing deformation was performed. The results showed that with rise of drawing strain, iron-rich phases in the Cu-14Fe-0.05C alloy gradually change from irregularly distributed coarse dendritic phases in the as-cast state to slender fibrous ones distributed parallel along the drawing direction. The higher the strain is, the slender and denser the fibers are and the more uniform the distribution is. Moreover, more interface… Show more
Set email alert for when this publication receives citations?
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.