Study of Micro-Inclusion of 20g Steel

Abstract

According to the production process of 20g steel(120t BOF→ LF→ CC), some system analysis are introduced to research on the content of T[O] and [N] and the type, source, composition and quantity of micro inclusions in refining process, pouring process and casting billet. The results of the study show: the content of T[O] is 93.2ppm in the normal billet which is 37.8ppm more than that at steady state in the export of tundish. The content of T[O] is 140.5ppm in the compound casting billet which is 70.133ppm more than that at non-steady state in the export of tundish. The secondary oxidation of mould is serious at casting progress. In billet, the quality of CaS-SiO2-Al2O3 complex inclusion is the most, the quality of MnS inclusion is the second, and the quality of Al2O3 inclusion is the least. The sulphur content in micro-inclusion of billet is higher. The sulphur content in CaS-SiO2-Al2O3 complex inclusion is 3~15%, the sulphur content in MnS inclusion is 25%. The particle size of less than 10μm in micro-inclusions is the largest. The particle size of 0~5μm is about 60%, the particle size of 5~10μm is about 35%, the particle size of 10~15μm is about 5%. The average total volume rate of micro-inclusion is 0.149% in normal billet. The average total volume rate of micro-inclusion is 0.184% in compound casting billet which is 1.23 times than normal billet. The number of micro-inclusion is 36.5/ mm2 in normal billet. The number of micro-inclusion is 58.5/ mm2 in compound casting billet which is 60.27% higher than normal billet. The non-steady state casting has serious influence on billet cleanliness.