Structure and properties of mechanochemically synthesized dysprosium titanate Dy 2 TiO 5

Eremeeva, Zh. V.; Панов, В. С.; Myakisheva, L. V.; Лизунов, А. В.; Непапушев, А. А.; Сидоренко, Д. А.; Vorotilo, S.

doi:10.1016/j.jnucmat.2017.07.058

Cited by 8 publications

(1 citation statement)

References 27 publications

Supporting

Mentioning

Contrasting

Order By: Relevance

“…Currently, the number of materials science researches in the field of development of the new functional materials and technologies for producing finished products by powder metallurgy methods is rapidly rising [1]. The methods of sintering without loading or pressureless sintering (PS), hot isostatic pressing and mechanochemical synthesis are the most widespread in industry [2][3][4][5][6]. The main problem in production by the traditional technologies is the relatively high porosity of the final products, which significantly affects their strength characteristics.…”

Section: Introductionmentioning

confidence: 99%

Enhancing Mechanical Properties of Various Sintered Pellets with Nano-Additives

Nguyên

Konyukhov

Nguyen³

2021

DDF

View full text Add to dashboard Cite

The impact of Fe, Co, Ni nano-additives on the density, microhardness and bending strength was investigated for several sintered pellets. Fe, Co, Ni nanopowders (NP) were prepared in the size range 67-94 nm using chemical metallurgy techniques. These powders (0.5 wt. %) were dispersed into three sets of micron powders: Co (+0.5 wt. % Co NP); Fe (+0.5 wt. % Fe NP); Fe+0.5wt. % C (+0.5 wt. % Co and 0.5 wt. % Ni NP). Mixtures were further mixed and processed using a magnetic mill and a turbulent mixer. Sintering was carried out using spark plasma sintering (SPS) as well as pressureless sintering (PS). The densities of sintered pellets were found to increase by 2.5-3% (SPS) and 3-5% (PS) in the presence of nano-additives; corresponding increases in microhardness and bending strength were determined to be 7.9-11.1% and 17.9-38.7%, respectively. These results are discussed in terms enhanced packing due to interparticle sliding and the filling of free spaces with the nanodisperse phase.

show abstract