Structural and magnetic properties of nickel nanowires grown in porous anodic aluminium oxide template by electrochemical deposition technique

Synthesis of nickel nanowires (Ni-NWs) as high ferromagnetic material by electrodeposition technique

“…It is interesting to note that the value of Ms is approximately the same but the value of Mr/Ms is found to be 0.2 times of parallel configuration value. The values of above parameters are in good agreement with the reported values [ 28 ]. It is also known that the value of Hc for Ni- NWs is greater than bulk nickel [ 32 ].…”

“…The value of “ a ” for (220) plane is equal to 3.495 Å. XRD results shows that the average values of “ D ” and “ a ” are decreased with the increasing M of nickel sulphate hexahydrate. The XRD results are well matched with the values reported by Pratama et al [ 28 ]. The development of diffraction planes related to Ni phase is in good agreement with the standard data (see Figure 4 ).…”

“…It worth noticing that the deposition rate is also associated with the increase of substrate surface transient temperature which affects the D values of synthesized films like Zirconia and ZrON. Different research groups have also reported that the structural parameters like micro-strains, stresses and defects are affected by the increase of substrate surface transient temperature [ 28 , 29 , 30 ]. Moreover, Labchir et al [ 31 ] have studied the Co and Ni nanowires synthesized by magneto-electrodeposition process and discussed their structural parameters.…”