Spectroscopic Properties from Er3+/Yb3+ Co-doped Tellurite Glass and Fiber

Abstract

Based on the analysis of optic spectrum to the rare earth doped glass and fabrication technique, the Er3+/Yb3+ codoped tellurite glass and its single-mode glass fiber are detailedly described here. Under exciting of 975nm LD laser, a broad ASE (amplified spontaneous emission emitting) in range of 1450 nm to 1650 nm is observed independence of the pumping laser power. Then, an approximate quasi-analytical model and rate equations with exact numerical solutions show good agreement with the experiments to the fiber ASE. Lastly, an "optimum design" of ASE intensity to the fiber length is discussed. The discussions will benefit the design of ASE lasers as well as to the noise analysis of Er3+ doped tellurite glass fiber amplifiers.

Caracterização experimental de fibras de vidro telurito dopado com érbio e itérbio

“…Em 2006, outra equipe de pesquisadores obtiveram resultados interessantes por meio da elaboração de um modelo com equações quase analíticas e soluções numéricas exatas de acordo com dados experimentais de emissão espontânea amplificada na faixa de 1.450 a 1.650 nm, com o objetivo de alcançar o comprimento ótimo da mais alta intensidade gerada por uma fibra de telurito dopado com 25.000 ppm de itérbio e 5.000 ppm de érbio. A máxima fluorescência foi obtida para uma amostra de 55 cm de comprimento, quando a potência de bombeio acoplada foi de 574 mW [21]. Em 2008, novos resultados foram obtidos por outro grupo, com amostras de 30 cm de comprimento, que exibiram uma de figura de ruído mínima de 4,8 dB em 1.557 nm, atuando em uma faixa de 50 nm sob uma potência de bombeio de 120 mW [22].…”