Solvent Extraction Characterization on Injection Molding of Mg Alloy

Abstract

Abstract. The effect of the leaching time and temperature on the solvent debinding process of Mg metal injection molding (MIM) green part has been investigated. In this study, both soluble binder, paraffin wax and stearic acid molecules were removed from the Mg MIM green part by immersing compact parts in heptane solution. Then, the solvent debinding rate has been investigated under the conditions of different leaching time and temperature. The weight loss percentages of paraffin wax and stearic acid were calculated and the pores structure was analyzed by scanning electron micrograph. The efficient diffusivity and activation energy of the soluble binder have also been studied. Result shows that the removal of soluble binder at high temperature is the fastest, but there are defects observed on the Mg MIM body. It was found that the total amount of binder removal was 68.24 wt.%, 75.56 wt.%, and 84.92 wt.% for leaching temperature of 40 ºC, 60 ºC, and 80 ºC, respectively. The remaining binder will be removed during first cycle of sintering process.

The investigation of the effects of debinding time and dimensions of sample on parts produced from tungsten carbide by powder injection molding

“…Literatürdeki diğer çalışmalarda da bağlayıcı ayırma süresinin artması ile ağırlık kaybının arttığı görülmüştür [10,[15][16][17]. Heng ve arkadaşlarının yaptığı çalışma gibi bu çalışmada da WC-% 9Co besleme stoğu için bağlayıcı ayırma işleminde ağırlık kaybı, bekleme süresi ile doğru orantılı değişmiştir.…”

“…Ayrıca Oliveira ve Chen çalışmalarında parça kalınlığının bağlayıcı ayırma sürecinde ağırlık kaybına etkisinin olduğunu tespit etmişlerdir. Parça kalınlığının artması ile ağırlık kaybının azaldığını belirtmişlerdir [6,17]. Bu çalışmada da parça kalınlığının artması ile bağlayıcı ayrıştırma süresinin artması gerektiği görülmüştür.…”