Single‐crystalline porous NiO nanobiscuits with prompt adsorption activity for Congo red

Abstract

Single-crystalline two-dimensional (2D) nickel oxide (NiO) porous nanobiscuits with diameters of 100-210 nm, thicknesses of 10-20 nm and pore sizes of <20 nm are fabricated through a low-cost water bath combined with calcination treatment approach. The composition and morphology of the products are characterised by X-ray diffraction, field-emission scanning electron microscopy, transmission electron microscopy (TEM), high-resolution TEM, selected area electronic diffraction and N 2 adsorption/desorption. The possible formation mechanism of single-crystalline porous NiO nanobiscuits is simply discussed. Served as adsorbent, the as-prepared single-crystalline porous NiO nanobiscuits exhibited excellent performance for the fast removal of Congo red from water, which is far beyond the adsorption rate of activated carbon. The results show that the adsorption isotherm fits well with Langmuir adsorption model. The maximum adsorption capacity is calculated to be 193.2 mg g −1 , which is larger than that of other reported 2D NiO architectures.

Nickel Oxide (NiO) Thin Film Synthesis via Electrodeposition for Methylene Blue Photodegradation

“…Figure 3 shows the XRD pattern of single-phase NiO appearing peak at 2θ = 43, 28°, by the ICDD standard data card # 01-078-0423 [25]. The strong and sharp diffraction peak indicates good crystallinity [26]. In addition, diffraction peaks of Cu substrate appeared at θ = 50.41° and 74.28° according to ICDD data 01-085-1326 [27].…”

Synthetic NiO catalyst‐assisted peroxymonosulfate for degradation of benzoic acid from aqueous solution

“…NiO is a promising transition metal oxide because of its advantages of low cost, environmental compatibility, and high chemical and thermal stability (Zheng et al, 2017). In practice, NiO particles are synthetized by various chemical and physicochemical technologies (Hu, Wang, Xuan, Zhang, & Xu, 2017) and have been employed in many fields such as supercapacitors (Cheng et al, 2015), lithium-ion batteries (Jadhav, Thorat, Mun, & Seo, 2016), gas sensors (Tian, Wang, Li, Nadimicherla, & Guo, 2016), adsorption (Zheng et al, 2017), and catalysis (Ye et al, 2016).…”

In-situ Synthesis rGO/NiO Nanorod Nanocomposites Via One-Step Hydrothermal Method and Investigating Physical Properties of Nanocomposites

“…Kết quả tính toán cho thấy, dung lượng hấp phụ của các mẫu DT00, DT05, và DT10 tương ứng với chất nhuộm MO là 9,7, 10,7, và 12,4 (mg/g); tương ứng với chất nhuộm RC là 195,0, 217,5 và 202,5 (mg/g). Kết quả này cho thấy, cả mẫu tổ hợp rGO@NiO (DT05 và DT10) và mẫu NiO thuần (DT00) có dung lượng hấp phụ RC là cao so với các cấu trúc hay tổ hợp NiO/Gr đã công bố[25][26][27]. Cụ thể, tổ hợp NiO/Gr tổng hợp bởi nhóm của Rong và cộng sự[27] cho dung lượng hấp phụ RC là 124mg/g.…”

“…Trong khi đó, NiO có hình thái dạng tấm nano và hạt nano chế tạo bởi Cheng và cộng sự[26] có dung lượng hấp phụ RC tương ứng là 151 và 40 mg/g. Với NiO dạng tấm nano xốp, Hu và cộng sự công bố dung lượng hấp phụ RC là 194 mg/g[25]. Như vậy, so với các kết quả đã công bố, mẫu DT05 cho dung lượng hấp phụ RC lớn và cho thấy khả năng ứng dụng trong xử lý chất nhuộm màu RC.…”