PURPOSE
This study aimed to assess the influence of various micromechanical surface conditioning (MSC) strategies with or without coupling agent (silane) application on the micro-shear bond strength (µSBS) of resin- matrix ceramics (RMCs).
MATERIALS AND METHODS
GC Cerasmart (GC), Lava Ultimate (LU), Vita Enamic (VE), Voco Grandio (VG), and Brilliant Crios (BC) were cut into 1.0-mm-thick slices (n = 32 per RMC) and separated into four groups according to the MSC strategy applied: control-no conditioning (C), air-borne particle abrasion with aluminum oxide particles (APA), 2W- and 3W-Er,Cr:YSGG group coding is missing. The specimens in each group were further separated into silane-applied and silane-free subgroups. Each specimen received two resin cement microtubules (n = 8 per subgroup). A shear force was applied to the adhesive interface through a universal test machine and µSBS values were measured. Data were statistically analyzed by using 3-way ANOVA and Tukey HSD test. Failure patterns were scrutinized under stereomicroscope.
RESULTS
RMC material type, MSC strategy, and silanization influenced the µSBS values (
P
<.05). In comparison to the control group, µSBS values increased after all other MSC strategies (
P
<.05) while the differences among these strategies were insignificant (
P
>.05). For control and APA, there were insignificant differences between RMCs (
P
>.05). The silanization decreased µSBS values of RMCs except for VE. Considerable declines were observed in GC and BC (
P
<.05).
CONCLUSION
MSC strategies can enhance bond strength values at the RMC - cement interface. However, the choice of MSC strategy is dependent on RMC material type and each RMC can require a dedicated way of conditioning.