Self‐Sealed Polyamide (PA)/Zinc Imidazole Framework (ZIF) Thin Film Nanocomposite (TFN) Nanofiltration Membranes with Nanoscale Turing Type Structures

Abstract

Polyamide (PA) thin‐film composite (TFC) nanofiltration (NF) membranes with superior water permeating nanoscale Turing type networks are formed using preloaded zinc(II) cations as diffusion slower during the interfacial polymerization on polysulfone support. Large nanopores in the size of about 4.3–8.0 Å formed during the interfacial polymerization process are self‐sealed by in situ grown zinc imidazole framework (ZIF) nanocrystals in a counterdiffusion polymerization reaction of Zn(II) cations with imidazole ligands. PA/ZIF mixed matrix NF membranes with superior water permeating networks are formed. Such novel membranes show not only 3–4 fold higher water flux than TFC membranes, but also retain comparably high salt rejection and antifouling resistance capability. The impact of Zn(II) loading levels, counterdiffusion reaction times, and structures of imidazole ligands on the structures and properties of formed TFN‐ZIF membranes are studied.

Recent progress in nanomaterial-functionalized membranes for removal of pollutants

“…Mechanism of (C) Ag NPs and (D) hydrophilic silica induced nanochannels in the PA layer for efficient water transport. Reproduced with permission from Yang et al. (2019a , 2019b) and Yin et al.…”

“…In recent years, it has become clear that the deadly impact of pharmaceutical effluent on the environment, particularly the widespread overuse of antibiotics, would have unforeseen repercussions ( Le et al., 2018 ; Wang et al., 2019b ). As a result, several researchers have presented a strategy against antibiotic waste via the composite membrane ( Shakak et al., 2020 ; Yang et al., 2019a , 2019b ). Karimnezhad et al.…”

An Evolving Insight into Metal Organic Framework-Functionalized Membranes for Water and Wastewater Treatment and Resource Recovery

“…ZIF-8 Based TFN Membranes . Zeolitic imidazolate frameworks such as ZIF-8 have been studied by a variety of groups for applications in RO and nanofiltration membranes. ,,,,, The ZIF-8 structure contains 3.4 Å pores that are capable of separating water molecules from hydrated sodium ions based on size differential, as water molecules and hydrated Na + ions have diameters of ∼2.75 Å and ∼7.20 Å, respectively. The addition of ZIF-8 can result in improved water flux and biofouling resistance, but the membrane performance depends strongly on ZIF-8 particle size and loading level, membrane fabrication method, functionalization of the ZIF-8 particles, and on the type of porous support membrane used.…”

Recent Developments in the Rational Fabrication of Thin Film Nanocomposite Membranes for Water Purification and Desalination

“…The high rejection for Na 2 SO 4 was achieved due to the self-sealing of almost all larger nanopores without creating extra interphasal defects after the completion of the counterdiffusion self-sealing reaction process. 35 The water desalination performance of HZNCs containing TFN membranes was assessed by filtering an individual salt (NaCl, Na 2 SO 4 , or MgSO 4 ) solution. The water desalination performance of the respective membranes was tunable with the loading amount of HZNCs in the PAselective layer.…”