Response Surface Methodology for Formulating PVA/Starch/Lignin Biodegradable Plastic

Abstract

The use of petroleum-based plastics has raised environmental issues as more plastic waste enters and accumulates in the environment. It has led to the development of biodegradable plastics. Starch is one of the potential materials to make biodegradable plastic, but starch-based plastic has poor mechanical strength. Blending starch with poly(vinyl alcohol) (PVA) and lignin is expected to improve the mechanical properties of the plastic. Biodegradable plastic films from PVA/starch/lignin blends with glycerol as a plasticizer were prepared using an internal mixer for compounding and a hot press molding machine for film making. The percentage of lignin (2-10%), glycerol (25-65%), and mixing temperature (190-230 oC) were varied according to the three levels of the Box-Behnken design. The ANOVA evaluation revealed that glycerol had the most significant effect on the mechanical properties of the film. Then, three models for the estimation of tensile strength, elongation at break, and tear resistance were developed. As expected, the models satisfactorily predict the effect of all input variables on the response variables. The optimum conditions for preparing the film were acquired from the equations, namely 197.6 oC for the temperature, 10% for lignin, and 45.1% for glycerol. The biodegradable plastic prepared using the optimum conditions possessed a tensile strength of 8.46 ± 1.08 MPa, an elongation at break of 139.00 ± 8.59%, and a tear resistance of 69.50 ± 2.50 N/mm. These values are in good agreement with the predicted values. Doi: 10.28991/ESJ-2022-06-02-03 Full Text: PDF

Investigating the Influence of Precursor Concentration on the Photodegradation of Methylene Blue using Biosynthesized ZnO from Pometia pinnata Leaf Extracts

“…It was observed from the color change of methylene blue to almost colorless. The degradation process was evaluated by absorption at 663 nm 18 , which can be seen in Fig 5a. The decrease in the absorption curve indicates that the concentration of methylene blue reduces due to the ZnO catalyst 10 .…”

“…ZnO biosynthesis is often applied to the photodegradation of pollutant wastes (toxic dyes), one of which is methylene blue. This pollutant is widely used in industry because it is cheap and dissolves quickly in water and alcohol 17,18 . Methylene blue (C16H18C1N3S) is a very stable toxic aromatic hydrocarbon compound that is difficult to decompose naturally 19,20 .…”

A Green Way of Producing High Strength Concrete Utilizing Recycled Concrete

“…If the water-cement ratio of the original concrete is equal to or lower than that of the recycled concrete, the resulting compressive strengths will be similar to or even better than the original strengths. Conversely, if the water-cement ratio of the original concrete is higher, the compressive strengths of the recycled aggregate concrete may be lower [8,25,28]. In order to decrease our dependence on natural resources, there has been a growing trend in recent years to manufacture concrete using recycled concrete aggregate (RCA).…”

Investigation of Laser Cutting of Thin Polymethyl Methacrylate Sheets by Response Surface Methodology

“…Response Surface Methodology (RSM) and the Taguchi method are two of the approaches for the design of experiments (8)(9)(10). Khoshaim et al (11) investigated the laser cutting of PMMA sheets by a continuous CO2 laser.…”