Resistance to Cyclic Fatigue of Nickel-Titanium Files Immersed in Sodium Hypochlorite at Body Temperature

Abstract

Background/purpose. To assess the resistance to cyclic fatigue (CF) displayed by two nickel-titanium (NiTi) files, One Curve (OC) and ProTaper Gold (PTG), after their immersion in 2.5% sodium hypochlorite (NaOCl) solution at body temperature. Materials and Methods. Forty-five files from each brand were randomly assigned to three groups (n = 15) and subjected to the following: no immersion (control), 1-minute immersion, and 5-minute immersion in 2.5% NaOCl at 37°C. CF for all the files was tested within a well-lubricated stainless-steel artificial canal in a water bath at 37°C simulating body temperature. The procedure was video recorded, and the number of cycles to fracture (NCF) was calculated by multiplying the time taken to fracture, with the number of rotations per second. The data were analyzed for normality, and thereafter, one-way ANOVA with multiple Bonferroni was used as the post hoc test. Results. The resistance to CF of OC files was significantly higher than PTG files in all groups. In groups immersed in NaOCl for one minute, OC files showed significant drop in the CF resistance; PTG files showed a drop as well but not significantly. Both files demonstrated a significant drop in resistance to CF after immersion in NaOCl for five minutes compared to the control group. Conclusion. OC files were significantly more resistant to CF compared to PTG in all groups. Immersion in 2.5% NaOCl for 5 minutes significantly reduced the resistance to CF for all the files.

Effect of autoclave sterilisation and heat activated sodium hypochlorite irrigation on the performance of nickel-titanium rotary files against cyclic fatigue

“…The present study demonstrated an adverse effect of 2.5% NaOCl irrigation on the CFR of OC files. That was in agreement with Abuhulaibah et al [47] as they showed that 5 min file immersion in 2.5% NaOCl at body temperature significantly lowered the resistance of the OC files for cyclic fatigue. On the other hand, the current results disagreed with that reported by Ertugrul [19].…”

Influência do hipoclorito de sódio na resistência à fadiga cíclica em instrumentos rotatórios endodônticos de memória controlada de NiTi: uma avaliação experimental

“…O NaOCl, em diversas concentrações, tem sido utilizado para avaliar o efeito na resistência de instrumentos de NiTi e, quando em contato, tem apresentado resultados diversos 9 . Muito embora trabalhos apontem que o NaOCl não influencia a resistência à fadiga 18 , os dados da pesquisa demonstraram que, na comparação do mesmo sistema em condições ambientais diferentes (TruH2O e TruNaOCl; LogH2O e LogNaOCl) com sistemas diferentes nas mesmas condições ambientais (TruNaOCl e LogNaOCl), NaOCl afetou negativamente a menor resistência à fadiga dos instrumentos testados, concordando com outros estudos 4,9 . Portanto, a primeira hipótese nula deste trabalho foi rejeitada.…”

“…Adicionalmente, testes de fadiga realizados próximos à temperatura corporal afetam as propriedades mecânicas dos instrumentos endodônticos, uma vez comparadas em temperatura ambiente 3,7 , confirmando os achados deste trabalho em outros na literatura 9,22 . Instrumentos de NiTi tratados termicamente com alta porcentagem da fase martensítica possuem ganho em flexibilidade e melhora no desempenho em resistência à fadiga cíclica 23 quando comparados com ligas austenitas 7 .…”

“…A solução de hipoclorito de sódio (NaOCl), composto halogenado, é um dos principais irrigantes e utilizada para limpeza dos canais radiculares durante o tratamento endodôntico, sendo conhecida por sua ampla ação e espectro antimicrobiano, capacidade proteolítica, dissolução tecidual e de suas propriedades de desbridamento 8,9 .…”