Reliability Analysis of PAUT Based on the Round-Robin Test for Pipe Welds with Thermal Fatigue Cracks

Abstract

Thermal fatigue cracks occurring in pipes in nuclear power plants pose a high degree of risk. Thermal fatigue cracks are generated when the thermal fatigue load caused by local temperature gradients is repeatedly applied. The flaws are mainly found in welds, owing to the effects of stress concentration caused by the material properties and geometric shapes of welds. Thermal fatigue pipes are classified as targets of risk-informed in-service inspection, for which ultrasonic testing, a volumetric non-destructive testing method, is applied. With the advancement of ultrasonic testing techniques, various studies have been conducted recently to apply the phased array ultrasonic testing (PAUT) method to the inspection of thermal fatigue cracks occurring on pipes. A quantitative reliability analysis of the PAUT method must be performed to apply the PAUT method to on-site thermal fatigue crack inspection. In this study, to evaluate the quantitative reliability of the PAUT method for thermal fatigue cracks, we fabricated crack specimens with the thermal fatigue mechanism applied to the pipe welds. We performed a round-robin test to collect PAUT data and determine the validity of the detection performance (probability of detection; POD) and the error in the sizing accuracy (root-mean-square error; RMSE) evaluation. The analysis results of the POD and sizing performance of the length and depth of thermal fatigue cracks were comparatively evaluated with the acceptance criteria of the American Society of Mechanical Engineers Code to confirm the effectiveness of applying the PAUT method.

In-Line Inspection (ILI) Techniques for Subsea Pipelines: State-of-the-Art

“…It boasts the capability to detect cracks as small as 25 mm in length with a minimum depth of 1 mm. and research have predominantly focused on the external inspection of pipeline welds [78][79][80], with relatively few examples of its use in Inline Inspection (ILI). But the application of PAUT technology in ILI has a well-established history.…”