Relationship of Rolling Reduction with Microstructure and Mechanical Properties of Cold-Rolled Ti-20V-4Al-1Sn Alloy

Abstract

This study was conducted to investigate the relationship of rolling reduction with the microstructure and mechanical properties of cold rolled Ti 20V 4Al 1Sn alloy. Cold rolling was performed under the rolling reduction between 10 50. The microstructure was compressed by cold rolling, and became finer. Plastic deformation was partially inhomogeneous in the thickness direction of the cold rolled material. The preferred orientation of the formed crystallographic texture was {112} 〈110〉 ～ {001} 〈110〉which is typical in metals possessing the bcc structure. The texture evolved with increasing rolling reduction. Hardness and static strength were increased by increase in rolling reduction because of work hardening and microstructural refinement. Anisotropy was induced in yield strength and work hardening exponent by cold rolling; however, it was not marked in hardness and tensile strength.

Influence of Cold Rolling on Fundamental Properties of Ti-15V-3Cr-3Sn-3Al Alloy

“…16,17) In previous studies, we examined the influence of cold rolling reduction and subsequent aging on the microstructure, hardness and mechanical properties of Ti-20V-4Al-1Sn alloy. 11,18) For engineering applications, however, it is important to further accumulate data concerning the influence of cold rolling on the fundamental properties. From the above viewpoint, Ti-15V-3Cr-3Sn-3Al alloy, having a different chemical composition from Ti-20V-4Al-1Sn alloy, was used as the substrate in this study.…”