Relationship between the reactions of hydrogen sorption/desorption and methanol oxidation on bifunctional Ni/Pd electrode in alkaline solution

Abstract

The present paper is aimed at studying the influence of the hydrogen sorption/desorption process occurring on the layered nickel-palladium (Ni/Pd) electrode on the kinetics of the reaction of methanol oxidation in strong alkaline KOH solution. The electrodes were prepared by chemical deposition of a thin layer of porous palladium on a nickel foam support. A scanning electron microscope was used for studying the morphology of both the nickel support and the porous palladium layer. The mechanism of the anodic desorption of hydrogen changes depending on whether or not 6 M KOH electrolyte is admixed with methanol. It was shown that, in the first cycle of the cyclic voltammetry (CV) measurements, the anodic peak current and peak charge related to the oxidative desorption of hydrogen significantly decrease due to the presence of methanol in KOH. This effect is attributed to the obstacles in hydrogen sorption due to the formation of a passivating layer on the Pd surface composed of both adsorbed methanol molecules and the intermediate products involving adsorbed CO. On the other hand, hydrogen desorbing from Pd electrode exerts influence on the kinetics of the reaction of methanol oxidation. Ni/Pd electrode undergoes considerable reactivation due to the potentiostatic saturation with hydrogen at −1.1 V, followed by the ease in hydrogen desorption. The CV measurements proved that, after such a treatment, the peak of hydrogen desorption partially overlaps the double peak of methanol oxidation and, in consequence, the rate of methanol oxidation is enhanced. The positive effect of hydrogen releasing from the electrode on the kinetics of the reaction of methanol oxidation is ascribed to the anti-poison behavior consisting in the reaction of hydrogen radicals with intermediates adsorbed on the Pd surface.

Preparation of a TiO2/PEDOT nanorod film with enhanced electrochromic properties

“…S4 †). 33 Compared with the sharp and narrow maximum oxidation peak of PEDOT, the maximum oxidation peak of TiO 2 /PEDOT showed obvious hysteresis. It showed that ions have hysteresis phenomenon in the deep doping process, the ions in the active layer will hinder the further doping anions, and the voltage needed to be increased to maintain the further doping process, so a wide oxidation peak phenomenon was generated.…”