Regulation of the Physical Characteristics of Titania Nanotube Aggregates Synthesized from Hydrothermal Treatment

Abstract

Titania nanotube aggregates with different porosities were prepared from hydrothermal treatment on commercial TiO 2 particles in NaOH followed by HCl washing. Pore structure analysis reflects that pores of smaller sizes are mainly contributed by the nanotubes while those of larger sizes are contributed by the interspace region of the aggregates. The hydrothermal treatment temperature, ranging within 110-150 °C, was shown to affect not only the extent of particle-to-sheet conversion, and thus the resulting structures of the nanotubes, but also the anatase-to-rutile transformation at high temperatures. The surface area of the nanotube aggregates increases with the treatment temperature to reach a maximum of ca. 400 m 2 /g at 130 °C, and then decreases with further increase of the temperature. In HCl washing, both the charge-removal rate and final state of the electrostatic charges on TiO 2 affect the rolling of TiO 2 sheets into nanotubes. This demonstrates that the nanotube structure can be regulated by adjusting the washing condition. Selective catalytic reduction of NO with NH 3 has been conducted to prove that the vast surface of the nanotube aggregates is accessible to the interacting molecules.

Preparation of TiO<SUB>2</SUB> Nanotubes and Their Photocatalytic Properties in Degradation Methylcyclohexane

“…After calcination at 450 C for 2 h, the TiO 2 nanotubes transformed to anatase, which was in good agreement with other studies. [17][18][19] Figure 2 shows the TEM images of the starting material and the prepared TiO 2 nanotubes. It can be seen the starting material exhibits nanoparticles type and the mean diameters are about 20 nm.…”

Partially nanowire-structured TiO2 electrode for dye-sensitized solar cells

“…4 (b). The pores ranging from ∼10 nm to more than 100 nm are mainly attributed to the interstitial spaces within the nanowire aggregates [40]. Note that there might be some co-existing nanotubes (in general, typical internal pore-size is ca.…”

“…• C [19,[40][41][42][43], which is close to the sintering temperature of DSC's porous electrode (∼500 • C).…”

Hydrothermal synthesis and properties of titania nanotubes doped with Fe, Ni, Zn, Cd, Mn

“…7) The intensity of reflections for hydrothermally modified TiO 2 structures is considerably less, while the half-width is higher than the analogical parameters of TiO 2 TC model. It is caused by insufficient crystallization of structures [28] and small amount of layers in the walls of nanotubes [29].…”