Recobrimentos à base de mulita em refratário de carbeto de silício obtidos a partir de PMSQ [POLI (METILSILSESQUIOXANO)] e alumínio

Abstract

Silicon carbide (SiC) presents low thermal expansion, high strength and thermal conductivity. For this reason it is used as kiln furniture for materials sintering. On the other hand, SiC degrades at high temperature under aggressive atmosphere. The use of protective coatings can avoid the right exposition of SiC surface to the furnace atmosphere. Mullite can be a suitable material as protective coating because of its high corrosion resistance and thermal expansion coefficient matching that of SiC (4,7 x10-6 /°C e 5,3 x10-6 /°C, respectively). In the present work a mullite coating obtained from ceramic precursor polymer and aluminium powder was studied to be applied over SiC refractories. Compositions were prepared with 10, 20, 30 and 50% (vol.) of aluminium powder added to the polymer. They were used aluminium powders with different distributions sizes These compositions were heat treated at different thermal cycles to determine a suitable condition to obtain a high mullite content. The composition with 20% of the smaller particle size Al powder was selected and used to be applied as a suspension over SiC refractory. The applied suspension, after dried, crosslinked and heat treated, formed a mullite coating over SiC refractory. Cycles of thermal shock were performed in coated and uncoated SiC samples to compare each other. They were carried out 26 cycles of thermal shock, in the following conditions: 600°C/30 min. and air cooling to room temperature. After each thermal shock, samples were analised by mean of optical and electron microscopy, elastic modulus was also determined. After thermal shock cycles the coating presented good adhesion and no significant damage were observed.