Quality evaluation of soil-cement-plant residue bricks by the combination of destructive and non-destructive tests

Abstract

A B S T R A C TResidues from agricultural activity can be used to improve the quality of soil-based bricks, constituting an interesting alternative for their destination. The technical quality of soilcement-plant residue bricks was evaluated by the combination of non-destructive and destructive methods. A predominant clayey soil, Portland cement and residues of husks of both rice and Brachiaria brizantha cv. Marandu (0, 10, 20, 30 and 40%, in mass, in substitution to the 10% cement content) were used. The bricks were submitted to destructive (water absorption and compressive strength) and nondestructive (ultrasound) tests for their physical and mechanical characterization. Results from both destructive and non-destructive tests were combined to determine the quantitative parameter named "anisotropic resistance" in order to evaluate the quality of the bricks. The addition that promoted best technical quality was 10% residue content, regardless of the residue type. The anisotropic resistance proved to be adequate for the technical quality evaluation of the bricks.Avaliação da qualidade de tijolos de solo-cimento-resíduos vegetais por meio da combinação de testes destrutivos e não-destrutivos R E S U M OResíduos provenientes da atividade agrícola podem ser utilizados para a melhoria da qualidade de tijolos, constituindo-se como interessante alternativa de sua destinação. Avaliou-se a qualidade técnica de tijolos de solo-cimento-resíduos vegetais pela combinação de testes destrutivos e não-destrutivos. Utilizou-se um solo predominantemente argiloso, cimento CP II-F 32 e resíduos das cascas de arroz e de braquiária (Brachiaria brizantha cv. Marandu) nos teores (em massa) de 0, 10, 20, 30 e 40% em substituição ao teor de 10% do cimento. Os tijolos foram submetidos a ensaios destrutivos (absorção de água e compressão simples) e não-destrutivos (ultrassom) para sua caracterização físico-mecânica; em seguida, os resultados dos ensaios destrutivos e não-destrutivos foram combinados para se determinar o parâmetro "resistência anisotrópica" utilizado na avaliação da qualidade técnica dos tijolos, tendo sido obtido o melhor resultado com o teor de 10% de resíduo em substituição ao cimento, independentemente do tipo do resíduo. Concluiu-se que a resistência anisotrópica se mostra adequada para a avaliação da qualidade técnica dos tijolos.

Soil-cement bricks with insertion of scheelite-tailings: Mechanical behavior and physico-chemical evaluation of kneading water

“…The compositions fixed for making the specimens were determined from the amount of cement, composing 10% by weight (Ferreira & Cunha, 2017), with the 90% consisting of soil previously sieved in ABNT mesh n° 4 (4.76 mm) and depleted, seeking to disaggregate the larger grains to give clay properties to the soil by increasing the content of fines.…”

Caracterização De Corpos De Prova Solo-Cimento Incorporados Com Filtros De Cigarros

“…Com relação à incorporação de resíduos é possível citar vários autores, dentre eles: Azevedo et al, (2019) avaliou a resistência à compressão e absorção de água em blocos de solo-cimento com incorporação de até 10% de lodo da indústria de papel e celulose verificando resultados coerentes com normas técnicas estabelecidas. Ferreira & Cunha (2017), analisou tijolos solocimento com diferentes teores de resíduos de cascas de arroz e braquiária e verificou, para ambos os casos, que o teor de 10% foi o mais adequado. Leonel et al, (2017) analisou tijolos solo-cimento, incorporando com resíduos de areia provenientes de fundição e também obteve resultados compatíveis com a legislação, para esse material.…”