Properties of silica fume procured from natural diatomite and its usage in the production of vacuum insulation panels

Abstract

The article shows the results of the research of silica fume particles procured from diatomite from Atemar deposit by means of separating silicic acid from colloidal dissolved state into the sediment. The objective of the work was to define thermal-physical and structural characteristics of the silica fume. The research included IR-spectrometry, granulometry, thermal gravimetric analysis, X-ray structural analysis, optical microscopy, and small angle X-Ray scattering. As a result of the research, the silica fume was defined to predominantly consist of amorphous silicon dioxide and had the developed pore structure of particles. A large number of nanosized particles and pores decreases heat transmission and increases reactive capability, that gives opportunity of using the powder silica fume as an active agent in dry mixes and concrete composites, as a component of sponge-glass, and as a filler material in vacuum insulation panel

Diatomites and Opoka From Western Kazakhstan Deposits: Lithogeochemistry, Structural and Textural Parameters, Potential of Use

“…Такие материалы подвергаются дегидратации поверхностей и поровых систем различных масштабов при температурах до 300 °C. Структурные перестройки первичных частиц микрокремнеземов и их агрегатов отмечаются в диапазоне 600-1000 °C и выражены в виде эндо-и экзотермических максимумов [29].…”

Investigation of the influence of technological factors and compositions of binders on the strength characteristics of blast–furnace cement with magnetized ferromagnetic additives

“…Thus, even weak magnetic fields affect the chemical activity of reagents [19,20]. Furthermore, the influence of magnetic fields on the hardening of binders is considered in works [21][22][23][24][25][26][27]. In research results [28,29], it has been proved that both the magnetization of particles and their dispersed composition affect the strength characteristics of BFC.…”

Оптимизационно-Аналитическое Моделирование Технологических Режимов Производства Микрокремнезема Для Изоляционных Панелей Типа VIP

“…м, и она в основном закрывается теплоизоляционными материалами на основе минеральной ваты, стекловолокнистых изделий, пенополистирола. Однако, по мнению специалистов, эти материалы не отвечают требованиям экологии, пожарной безопасности, долговечности и надёжности [1][2][3]. В то же время перед строителями России поставлены задачи увеличения объёмов жилищного строительства в два раза и снижения удельного энергопотребления системой теплоснабжения до 35-40 Вт…”

“…Топология поверхности глобул характеризуется фрактальной размерностью D = 2,32; 2,64, что обеспечивает снижение значений коэффициента аккомодации и соответственно теплопроводности. Ассоциации шаровидных кластеров из частиц наноразмерного уровня формируют масштабно-инвариантную поровую структуру, обеспечивающую низкую теплопроводность 1 .…”