Properties of Multi-Function Micro-Plasma Sprayed Nanostructured Al₂O₃-13wt%TiO₂ Coatings

Abstract

Nonastructured Al2O3-13wt%TiO2 (AT13) coatings were deposited by multi-function micro-plasma spray and Metco 9M plasma spray, respectively. Constituent phases and the microstructure of the powder particles and coatings prepared were examined with the aid of scanning electronic microscope (SEM) and X-ray diffraction (XRD). Mechanical properties including hardness and bonding strength were also evaluated by microhardness tester and electron tensile tester. Multi-function micro plasma sprayed nanostructured AT13 Coating is fully-melted, dense and uniform. However, AT13 Coating deposited by Metco 9M plasma spray is partial-melted. The microhardness of multi-functional micro plasma sprayed AT13 Coating is HV975.7~1441.7, much higher than that of Metco 9M plasma sprayed AT13 Coating (HV655.3~946.6). The bonding strength results present the same, increased from 19.8 MPa to 42.7 MPa.