Preparation of Stable Colloidal Silica with Controlled Size Nano Spheres from Sodium Silicate Solution

Qomariyah, Lailatul; Sasmita, F N; Novaldi, H R; Widiyastuti, W.; Winardi, Sugeng

doi:10.1088/1757-899x/395/1/012017

Cited by 23 publications

(12 citation statements)

References 14 publications

Supporting

Mentioning

Contrasting

Unclassified

Order By: Relevance

“…Pengembangan sintesis silika nanopartikel dari sodium silikat (Na2SiO3) [6] telah dilakukan di departemen Teknik Kimia ITS. Karena itu dalam penelitian ini digunakan Na2SiO3 sebagai pengganti TEOS untuk mengurangi tahapan dalam sintesis silika nanopartikel, karena Na2SiO3 telah memiliki gugus silanol (Si-OH) yang diharapkan dapat membentuk ikatan dengan surfaktan walaupun tanpa penambahan bahan penyambung.…”

Section: Metode Penelitianunclassified

“…Sol silika hasil sintesis memiliki nilai zeta potensial sebesar -34,2 mV. Hal ini menunjukkan bahwa sol silika nanopartikel memiliki kestabilan yang baik dalam fase liquid, karena memiliki nilai zeta potensial lebih dari atau sama dengan absolut 30 [6]. Sol silika yang stabil dapat meminimalisir terjadinya aglomerasi, sehingga ukuran partikel silika dapat dipertahankan pada ukuran yang diharapkan.…”

Section: Hasil Dan Pembahasanunclassified

See 1 more Smart Citation

Peningkatan Stabilitas Busa dengan Nanofluida Silika Untuk Meningkatkan Produksi Gas Alam

et al. 2020

View full text Add to dashboard Cite

Pemanfaatan gas alam sebagai sumber energi alternatif masih belum optimal karena masalah beban cairan pada sumur gas, surfaktan merupakan solusi yang menjanjikan untuk mengatasi masalah tersebut, namun dengan kondisi sumur gas yang ekstrem diperlukan stabilizer untuk meningkatkan stabilitasnya. Penelitian ini mempelajari pengaruh pencampuran surfaktan dan stabilizer berupa silika (SiO2) nanopartikel yang disintesa dari sodium silikat (Na2SiO3) untuk mendapatkan kondisi optimum nanofluida SiO2 terhadap waktu paruh busa yang menunjukkan kestabilannya. Silika nanopartikel disintesa dengan metode sol-gel dan dipertahankan dalam fase koloid stabil yang kemudian didispersikan ke dalam larutan surfaktan tanpa perlu penambahan bahan penyambung. Nanofluida SiO2 kemudian dimatangkan dengan variasi waktu dan konsentrasi silika. Dari hasil yang diperoleh menunjukkan bahwa peningkatan waktu pematangan dan konsentrasi silika memengaruhi nilai tegangan permukaan yang berakibat menurunkan waktu paruh busa. Penurunan kestabilan busa terjadi karena peristiwa adsorbsi fisik molekul surfaktan oleh silika nanopartikel yang ditunjukkan oleh nilai tegangan permukaan, karena silika yang bersifat hidrofilik akan membentuk ikatan fisik dengan surfaktan, semakin meningkatnya waktu pematangan dan konsentrasi silika yang didispersikan kedalam larutan akan meningkatkan adsorbsi molekul surfaktan pada permukaan silika dan menyebabkan terjadinya peningkatan nilai tegangan permukaan nanofluida. Stabilitas busa terbaik diperoleh pada sampel dengan waktu pematangan selama 6 jam dan konsentrasi silika 0,001% menghasilkan waktu paruh selama 1170 menit yang jika dibandingkan dengan surfaktan tanpa penambahan silika nanopartikel hanya memeroleh waktu paruh selama 90 menit, sehingga penggunaan silika nanopartikel sebagai stabilizer memberikan efek yang signifikan terhadap kestabilan busa.

show abstract

Section: Metode Penelitianunclassified

Section: Hasil Dan Pembahasanunclassified

Peningkatan Stabilitas Busa dengan Nanofluida Silika Untuk Meningkatkan Produksi Gas Alam

et al. 2020

View full text Add to dashboard Cite

show abstract

“…Silica sol was synthesized by ion exchange method using resin Amberlite as ion exchanger and sodium silicate as the source of silicon. The process of synthesizing sol silica consists of the following steps [14,15]:…”

Section: Synthesis Of Silica Solmentioning

confidence: 99%

Flame retardancy improvement of modified cotton fabric by nano silica sol coating

Trang

et al. 2020

Vietnam J. Sci. Technol.

View full text Add to dashboard Cite

Cotton fabric was coated by silica sol at different times using dip-coating method. Nano silica coated fabrics were characterized by XRD, FTIR, SEM, EDX, TGA. From SEM result, it showed that fabric surface was coated by nanosilica particles of 20-30 nm size. Nano silica coated fabrics showed the improvement not only flame retardancy (LOI increased from 18.4 to 30.8) but also the tear strength. Tear strength increased from 23 N/mm (cotton fabric) to 29.9 N/mm (fabric coated nanosilica at 3 times).

show abstract

“…Flame retardants of inorganic nature such as nanosilica, nano alumino-silica, nano clay are often used to cover the fabric surface to create an insulating and fireproof protective layer and simultaneously, the physico-mechanical properties can be improved. Among inorganic flame retardants, nano silica and nano titanium dioxide have received a great interest because these materials are environmentally friendly, non-toxic and highly effective in slowing or resisting fire [9][10][11][12]. El-Shafei et al [13] modified the fabric with nano TiO 2 sol gel from titanium isopropoxide and the fire resistance of the TiO 2 modified fabric is significantly improved (LOI increased from 17.4% to 23%).…”

Section: Introduction *mentioning

confidence: 99%

High Flame Retardant Performance of SiO2-TiO2 Sol Coated on Polyester/Cotton Fabrics

Trang

Giang

Manh

et al. 2021

NST

View full text Add to dashboard Cite

SiO2 and TiO2 sols were successfully synthesized by using sodium silicate and titanium chloride as Si and Ti sources. SiO2-TiO2 sol coated polyester/cotton fabric was fabricated by deep-coating method and using SiO2, TiO2 sols as coating materials. SiO2-TiO2 coated fabric were characterized by XRD, FTIR, TGA, SEM and EDX. From SEM image, it showed the SiO2, TiO2 particles of 20-30 nm which well deposited on fabric surface. TGA result revealed the significant improvement of thermal resistance and stability of SiO2-TiO2 coated fabric as compared to those of uncoated fabric. Flame retardant performance of SiO2-TiO2 coated fabrics was much better than that of uncoated fabric. Thus, SiO2-TiO2 coated fabric SiO2-TiO2 content of 26wt% showed the UL-94 classification of V-0 and LOI value of 30.3 were obtained. Moreover, mechanical property (tear strength) of SiO2-TiO2 coated fabrics were also improved.

show abstract

Preparation of Stable Colloidal Silica with Controlled Size Nano Spheres from Sodium Silicate Solution

Cited by 23 publications

References 14 publications

Peningkatan Stabilitas Busa dengan Nanofluida Silika Untuk Meningkatkan Produksi Gas Alam

Peningkatan Stabilitas Busa dengan Nanofluida Silika Untuk Meningkatkan Produksi Gas Alam

Flame retardancy improvement of modified cotton fabric by nano silica sol coating

High Flame Retardant Performance of SiO2-TiO2 Sol Coated on Polyester/Cotton Fabrics

Contact Info

Product

Resources

About