Preparation, Characterisation, and Application of Bifunctional BaSO4 Sheets

Abstract

Barium sulfate (BaSO4) is a material with high reflectance for preparing bifunctional sheets used in dry reagent chemical tests. In this study, bifunctional BaSO4 sheets with scattering power and high reflectance were prepared with BaSO4 microspheres sized 1.3~1.8 μm and cellulose acetate (CA). Factors such as the BaSO4 morphology, CA dosage, mixing time, surfactant, solid content and wet sheet thickness were investigated. Scanning electron microscopy (SEM), a dynamic contact angle test, light reflection detector and light reflection densitometer were employed to characterize the structure and properties of bifunctional BaSO4 sheets. The optimal conditions for preparing bifunctional BaSO4 sheets under natural drying conditions were as follows: mass ratio of CA to BaSO4 microspheres was 0.03:1; mixing acetone solution was used to form liquid stock puree; 35 μL Tween-80 was used to improve the hydrophilicity of bifunctional sheets; solid content was 54.9%; mixing 2 h then 450 µm thick sheets were cast on a glass plate using a film applicator. The light reflectance value of bifunctional BaSO4 sheets in the range of 400~800 nm was higher than 97%. Serum diffused in bifunctional BaSO4 sheets reacted in reagent sheets and formed uniform colorful spots. Considering the repeatability of spot proportion and light reflectance value, the sheet offered a uniform serum scattering power and good repeatability. Therefore, the bifunctional BaSO4 sheets are regarded as a promising material for dry chemical diagnostic reagents.

Production of Bone Cement Composite from Polymethyl Methacrylate Produced in Laboratory Scale

“…There is no significant effect on BaSO4 content both on low or high MMA content samples on the morphology of bone cement. This might be because the particle size of BaSO4 [8] was much smaller than the bone cement matrix. From the spectra can be used for the calculation of the tacticity and the residual monomer from the H-NMR spectra can be seen in Table 1.…”