Preparation and properties of waterborne dual curable monomers and cured hybrid polymers for ink-jet applications

A series of waterborne polyurethane (WPU) microemulsions were synthesized through self‐emulsification methodology, using toluene‐2,6‐diisocyanate, polytetramethylene glycol (PTMG), poly‐caprolactonediol (PCL), and dimethylol propionic acid (DMPA) as monomers; isophorone diamine (IPDA) as chain extender; and aziridine as cross‐linking agent. The resultant WPU microemulsions were utilized as surface‐sizing agents for cellulose fiber paper. The influences of IPDA content, PTMG/PCL molar ratio, and aziridine content on the physicochemical properties of the resultant emulsions and sized paper have been investigated in detail. The WPU microemulsion displayed better surface sizing properties when it was prepared under the following conditions: the IPDA content of 2.96%, PTMG/PCL molar ratio of 0:4, and aziridine content of 2.0 wt %. The relationships between the WPU structure and properties of WPU films and sized paper were clearly illustrated. The mechanical properties and water resistance of sized paper were not only depended on the interactions, chain entanglements, and cross‐linking density among the WPU chains, but also relied on the interactions among polymers and fibers, as well as the polarity and stiffness of surface sizing agent. © 2015 Wiley Periodicals, Inc. J. Appl. Polym. Sci. 2016, 133, 43211.

Section: Introductionmentioning

confidence: 99%

Properties and paper sizing application of waterborne polyurethanemicroemulsions: Effects of extender, cross‐linker, and polyol

Zhu

Wang

et al. 2016

“…Incorporation of inorganic filler helps to enhance the mechanical and thermal properties of the composite materials. The composite can be prepared by addition of inorganic filler or in situ sol–gel reactions of dual curable monomers . Since dental composite resins were invented, the most important changes have involved improving the filler and the mechanism of initiation, which has been developed to produce materials that are more easily handled and demonstrate better clinical performance .…”

Section: Introductionmentioning

confidence: 99%

Composite resins based on novel and highly reactive bisglycidyl methacrylate monomers

Herrera‐González

D’Accorso

Cuevas‐Suárez

et al. 2014

Three new bisglycidyl monomers; 1,4‐bis((2‐hydroxy‐3‐methacryloxypropoxy) methyl)benzene (MB‐Phe‐OH), 1,4‐bis(2‐hydroxy‐3‐methacryloxypropoxy)2‐cis‐butene (MB‐Cis‐OH), and 1,7‐bis(2‐hydroxy‐3‐methacryloxypropoxy)heptane (MB‐1,7‐OH); were synthesized and used as Bis‐GMA/TEGDMA (bisphenolglycidyl methacrylate/triethylene glycol dimethacrylate) composite resin additives. Flexural properties and double bond conversion of the dental resins composed of silanizated inorganic filler and organic matrices containing new monomers were evaluated. The composite resins formulated, using the monomers MB‐Cis‐OH and MB‐1,7‐OH, have mechanical properties and double bond conversion comparable with those of Bis‐GMA/TEGDMA composite resin used as control. The composite containing the new monomer MB‐Phe‐OH has better flexural properties (flexural strength 65.01 MPa and flexural modulus 5675.91 MPa) than the control composite resin (flexural strength 52.85 MPa and flexural modulus 4879.72 MPa); this could be attributed to the molecular structure of the monomer and its high double bond conversion level of 74.19%. The new bisglycidyl methacrylate monomer MB‐Phe‐OH could be potentially useful in the development of new organic matrices for dental composite resins with high double bond conversion and enhanced mechanical properties. © 2014 Wiley Periodicals, Inc. J. Appl. Polym. Sci. 2014, 131, 40971.

“…Waterborne polyurethanes (WPUs) are an important group of materials that have been widely used in environmental coatings, adhesives, inks, and intelligent materials because of their outstanding mechanical properties, adhesive properties, and shape‐memory functions . In general, polyurethanes (PUs) can be treated as segmented polymers that consist of hard segments (HSs) and soft segments (SSs).…”

Section: Introductionmentioning

confidence: 99%

Crystallinity evolution of soft segments during the synthesis of polyester‐based waterborne polyurethane

Cao

Xia

Liu

et al. 2013

Polyester‐based waterborne polyurethane (WPU) dispersions having poly(ethylene glycol) adipate diol, isophorone diisocyanate, and hexamethylene diisocyanate as the main raw materials were synthesized by an acetone process. In each step of the synthesis process, the intermediate products were collected, and the crystallization morphologies and relative crystallinity (X) of the soft segments (SSs) in their films were investigated by means of polarizing optical microscopy, differential scanning calorimetry, and X‐ray diffraction. The fracture surfaces and thermostability of the intermediate films were also investigated by scanning electron microscopy (SEM) and TGA, respectively. The results show that the crystalline dimensions of the SSs decreased substantially during the synthesis process of WPU. X of the SSs decreased after the prepolymerization reaction and increased after the hydrophilic chain‐extending reaction, then decreased after emulsification, and finally increased after the secondary chain‐extending reaction. Moreover, The SEM photos indicate that with decreasing crystalline dimensions, the fracture mechanisms of the intermediate films varied gradually from brittle failure to ductile fracture. The thermostability of the intermediates obtained in each step of the synthesis process was in accordance with the variation tendency of the X of the SSs. © 2013 Wiley Periodicals, Inc. J. Appl. Polym. Sci. 2014, 131, 40270.