The temperature dependence of the yield-stress of mono-and poly-crystalline a-brasses containing 5 to 35 atyo zinc in the range 4 to 300 K is analysed in terms of the kink-pair model of solid-solution hardening. The parameter W, in the theoretical relation t = to exp ( -mkT/W,), where m is a constant equal to about 25, is evaluated for each composition of brasses from the slope of the In t / Tline drawn through data points. A peak is observed at about 27 atyo zinc in the correlation of W, with solute concentration c. The decrease in the value of W, with increase in c beyond 27 a t yo zinc seems to be associated with short-range order in the vicinity of dislocation cores. Mit dem Knotenpaarmodell der Mischkristallhiirtung wird die Temperaturabhangigkeit der FlieBspannung von ein-und polykristallinem a-Messing mit 5 bis 35 at% Zink im Bereich von 4 bis 300K analysiert. Der Parameter W, in der theoretischen Beziehung t = to esp (-mkT/W,), wobei m eine Konstante ist (= 25), wird fiir jede Messingzusammensetzung aus dem Anstieg der In t / T -Kurve durch die MeBpunkte berechnet. Ein Maximum wird bei etwa 27 at% Zink in der Korrelation von Vo mit der Konzentration c beobachtet. Der Abfall von W , mit dem Anstieg von c oberhalb 27 at% Zink scheint mit der Nahordnung in der Niihe von Versetzungskernen verkniipft zu sein.