Polypropylene/wood powder composites: Evaluation of PP viscosity in thermal, mechanical, thermomechanical, and morphological characters

Abstract

Large waste amounts from wood industries as powder and sawdust are daily produced, and reusing these materials otherwise would be discharged to the environment has become an economically viable and environmentally friendly alternative to produce new materials. Based on these arguments, polypropylene (PP)/Jatobá wood powder composites upon addition of two types of PP were processed in a corotational twin screw extruder; specimens were injected and molded and their characterization was performed through differential scanning calorimetry, thermogravimetry, mechanical properties (impact, tensile, flexural, and hardness), heat deflection temperature (HDT), Vicat softening temperature, and scanning electron microscopy (SEM). Increased elastic modulus, shore D hardness, HDT, and Vicat related to neat PPs were reached. Nevertheless, losses in impact and tensile strength as well as in elongation at break were also verified. These lower data may be associated with the wood agglomeration, as shown in SEM images. Apparently, the investigated properties were not affected by PP viscosities, where both of them presented similar data. Summing up, presented results can be considered commercially feasible, focusing at economic and environmental benefits while producing higher performance products.

Production of Eco-Sustainable Materials: Compatibilizing Action in Poly (Lactic Acid)/High-Density Biopolyethylene Bioblends

“…Shore D hardness testing is performed at room temperature; solid PLA has high surface hardness (69). Regarding BioPE, it displayed low hardness as it is a material Similar to HDT, the Vicat softening temperature is considered an important property in polymeric systems, during production and projection of industrial applications aimed at thermomechanical resistance, being the temperature at which a needle penetrates the sample 1 mm, under a specific load, being mostly of materials, directly proportional to their surface hardness [53,56]. Figure 9 shows the relationship between VST and Shore D hardness of the investigated samples.…”

Biopolyethylene/Morinda citrifolia cellulosic biocomposites: The impact of chemical crosslinking and PE‐g‐MA compatibilizer

“…This feature is crucial to provide better mechanical anchoring to the polymer matrix, improving the mechanical properties when compared to particles with smooth surfaces. [56,57] 4.2 | Biocomposites characterization…”

Produção de biocompósitos de biopolietileno/farinha de madeira compatibilizados com PE-g-MA. Avaliação do teor de anidrido maleico nas propriedades mecânicas e termomecânicas

“…A análise termomecânica pode ser utilizada para avaliar a compatibilidade de compósitos poliméricos de forma semelhante às propriedades mecânicas (Silva et al, 2016;Ferreira et al, 2019). A temperatura de deflexão térmica (HDT) é uma propriedade importante para a área da tecnologia de polímeros, uma vez que mensura a estabilidade estrutural do material em temperatura acima da ambiente (Marinho et al, 2020;Luna et al, 2019c).…”