Polyacrylamide Hydrogel Enriched with Amber for In Vitro Plant Rooting

Abstract

In this work, a new material for in vitro plant rooting based on highly dispersed polyacrylamide hydrogel (PAAG) enriched with amber powder was synthesized and investigated. PAAG was synthesized by homophase radical polymerization with ground amber addition. Fourier transform infrared spectroscopy (FTIR) and rheological studies were used to characterize the materials. They showed that the synthesized hydrogels have physicochemical and rheological parameters similar to those of the standard agar media. The acute toxicity of PAAG-amber was estimated based on the influence of washing water on the viability of plant seeds (pea and chickpea) and Daphnia magna. It proved its biosafety after four washes. The impact on plant rooting was studied using the propagation of Cannabis sativa on synthesized PAAG-amber and compared with agar. The developed substrate stimulated the rooting of the plants to more than 98% in comparison to standard agar medium (95%). Additionally, the use of PAAG-amber hydrogel markedly enhanced metric indicators of seedlings: root length increased by 28%, stem length—by 26.7%, root weight—by 167%, stem weight—by 67%, root and stem length—by 27%, root and stem weight—by 50%. This means that the developed hydrogel significantly accelerates reproduction and allows obtaining a larger amount of plant material within a shorter period of time than the standard agar substrate.

Comparison of Structural, Water‐Retaining and Sorption Properties of Acrylamide‐Based Hydrogels Cross‐Linked by Physical and Chemical Methods

“…PAAm‐AAc hydrogel has the highest sorption capacity due to a large number of carboxyl groups, binds cadmium ions very strongly, and is incapable of releasing metals at neutral pH. Therefore, PAAm‐AN‐MMT could be considered the most promising for the prolonged release of compounds for future applications [70] …”

“…Therefore, PAAm-AN-MMT could be considered the most promising for the prolonged release of compounds for future applications. [70]…”

“…First of all, it is the heterogeneity of their structure and, as a consequence, low mechanical strength and elasticity [4] . Moreover, the synthesis of chemically cross‐linked gels requires toxic cross‐linking agents, which necessitates a further high‐cost procedure of washing them from unreacted starting materials [5–7] . These disadvantages severely reduce the quality of the product and the applications of these species.…”