Photocatalytic activity of TiO2/SiO2 systems

Bellardita, Marianna; Addamo, Maurizio; Paola, A. Di; Marcı̀, Giuseppe; Cassar, L.; Borsa, M.

doi:10.1016/j.jhazmat.2009.09.108

Cited by 118 publications

(75 citation statements)

References 37 publications

Supporting

Mentioning

Contrasting

Unclassified

Order By: Relevance

“…This indicated that SiO 2 modification can improve the adsorption capacity of TiO 2 catalyst. 22 Besides, the obvious difference in adsorption capacity between SiO 2 /TiO 2 and SiO 2 @TiO 2 hint that not the mechanical mixing but some interaction existed between SiO 2 and TiO 2 in SiO 2 @TiO 2 , which is consistent with the XPS and PL result.…”

supporting

confidence: 78%

Preparation of SiO₂-Coated TiO₂Composite Materials with Enhanced Photocatalytic Activity Under UV Light

Hu¹,

Li²,

Fan³

2012

Bulletin of the Korean Chemical Society

View full text Add to dashboard Cite

SiO 2 -coated TiO 2 composite materials with enhanced photocatalytic activity under UV light was prepared by a simple catalytic hydrolysis method. XRD, TEM, UV-vis spectroscopy, Photoluminescence, FT-IR and XP spectra were used to characterize the prepared samples. The obvious shell-core structure was shown for obtained SiO 2 @TiO 2 sample. The average thickness of the SiO 2 coating layer was 2-3 nm. The interaction between SiO 2 and TiO 2 restrained the recombination of excited electrons and holes. The photocatalytic activities were tested in the degradation of an aqueous solution of a reactive dyestuff, methylene blue, under UV light. The photocatalytic activity of SiO 2 @TiO 2 was much higher than that of P25 and mechanical mixing sample SiO 2 /TiO 2 . The possible mechanism for the photocatalysis was proposed.

show abstract

supporting

confidence: 78%

Preparation of SiO₂-Coated TiO₂Composite Materials with Enhanced Photocatalytic Activity Under UV Light

Hu¹,

Li²,

Fan³

2012

Bulletin of the Korean Chemical Society

View full text Add to dashboard Cite

show abstract

“…O dióxido de titânio também pode ser sinterizado em laboratório. A técnica mais utilizada é sol-gel a partir de um precursor como tetraisopropóxido de titânio [17][18][19][20][21][22] ou tetracloreto de titânio [23,24]. A utilização do tetraisopropóxido de titânio (Ti-i-pr, Ti(OCH(CH 3 ) 2 ) 4 ) como precursor é mais referenciada, na qual sóis aquosos de Ti-i-pr são obtidos a partir da peptização e hidrólise de Ti-i-pr usando água destilada.…”

Section: Produção Industrial E Síntese Em Laboratóriounclassified

“…A fotocatálise tem emergido como um processo de oxidação avançada (POA) para a descontaminação da água [24,42,49] juntamente com a remoção de micro-organismos como uma alternativa ao tratamento convencional de água potável, bem como para a produção de água ultrapura para aplicações farmacêuticas [50], compostos corantes [7,51], degradação de poluentes do ar, na obtenção de superfícies auto limpantes [52,53] na esterilização, e até mesmo na terapia do câncer [7,33] devido à geração de espécies oxidantes fortes.…”

Section: Ativação Fotocatalíticaunclassified

Superfícies fotocatalíticas de titânia em substratos cerâmicos: Parte I: Síntese, estrutura e fotoatividade

et al. 2013

View full text Add to dashboard Cite

ResumoA fotocatálise é um processo de oxidação avançada capaz de transformar uma grande variedade de poluentes orgânicos tóxicos em substâncias inofensivas em condições ambientes. Porém, a utilização do dióxido de titânio na fase anatase em produtos cerâmicos é limitada devido à transformação para fase rutilo em temperaturas superiores a 400 °C. As pesquisas apontam caminhos promissores para inibir a formação da fase rutilo através da introdução de dopantes na estrutura do semicondutor. Neste trabalho, foi realizada uma revisão dos principais aspectos encontrados na literatura especializada sobre fotocatálise com dióxido de titânio, em particular a relação entre estrutura química e atividade fotocatalítica. Palavras-chave: fotocatálise, dióxido de titânio, superfícies cerâmicas. Abstract Photocatalysis has been considered as an advanced oxidation process capable of transforming a large variety of toxic organic

show abstract

“…Different alternatives have been explored in order to overcome this issue. The use of bonding agents such as silica is one of the most attractive ideas due of its usability and low cost [15][16][17][18][19]. In this case, the linker has two functions: trap TiO 2 particles and strongly adhere them to the fabric, allowing UV light activation of the semiconductor.…”

Section: Introductionmentioning

confidence: 99%

Synthesis variables effect on TiO2/polyester fabrics photoactivity and stability

Velasco

Castro

Giraldo

2016

rev.ion

View full text Add to dashboard Cite

TiO 2 -SiO 2 coatings on fabric samples were obtained by immersion of 9cm 2 of commercial polyester in a TiO 2 -SiO 2 suspension. This suspension was prepared by adding TiO 2 P25 to a silica matrix obtained from the hydrolysis of tetraethyl orthosilicate (TEOS). The aim of this work was to study the relationship between the immersion time of the fabric on the photocatalytic activity and stability of the coating against several cycles of use and washing. Obtained samples were characterized by scanning electron microscopy (SEM), energy dispersive spectroscopy (EDS) and infrared spectroscopy (FTIR-ATR). Evaluation of modified fabrics was performed by self-disinfection tests under 250W/m 2 of simulated sunlight using E. coli as model bacteria. In general, all modified fabrics (except that obtained at 2h immersion time) inactivated bacteria in less than 120min and its regrowth was prevented for at least 24h after the disinfection tests. It was determined that low immersion time (3-4h) lead to active and stable fabrics to 3 cycles of use and washing, whereas higher immersion times (12h) lead to more active but unstable fabrics. Keywords: coated fabric, TiO 2 -SiO 2 , photocatalysis, E. coli inactivation. ResumenMuestras de tela recubiertas con TiO 2 -SiO 2 fueron obtenidas por inmersión de un poliéster comercial de 9cm 2 en una suspensión de TiO 2 -SiO 2 . Esta suspensión se preparó adicionando TiO 2 P25 a una matriz de sílice sintetizada mediante la hidrólisis de ortosilicato de tetraetilo (TEOS). El objetivo de este trabajo fue estudiar la relación entre el tiempo de inmersión de la tela, y la actividad fotocatalítica y estabilidad del recubrimiento a varios ciclos de uso y lavado. Las muestras obtenidas fueron caracterizadas por microscopía electrónica de barrido (SEM), espectroscopía de energía dispersiva (EDS) y espectroscopía infrarroja (FTIR-ATR). La evaluación de los textiles se llevó a cabo mediante pruebas de autodesinfección bajo 250W/m 2 de luz solar simulada usando E. coli como microorganismo modelo. En general, todas las telas modificadas (excepto las obtenidas con 2h de inmersión) inactivaron la bacteria en menos de 120min, previniendo su recrecimiento bacteriano al menos por 24h después de las pruebas de desinfección. Se determinó que los tiempos de inmersión bajos (3-4h) dejan telas activas y estables a 3 ciclos de uso y lavado, mientras que tiempos de inmersión más altos (12h) dejan telas más activas pero inestables. ResumoAmostras de tecido revestidas com TiO 2 -SiO 2 foram obtidos por imersão de um poliéster comercial de 9cm 2 em uma suspensão de TiO 2 -SiO 2 . Esta suspensão foi preparada por adição de TiO 2 P25 a uma matriz de sílica sintetizado por hidrólise de ortossilicato de tetraetilo (TEOS). O objetivo deste trabalho foi estudar a relação entre o tempo de imersão do tecido, e a atividade fotocatalítica e a estabilidade do revestimento a vários ciclos de utilização e de lavagem. As amostras obtidas foram caracterizadas por microscopia eletrônica de varredura (MEV), espectroscopia p...

show abstract

Photocatalytic activity of TiO2/SiO2 systems

Cited by 118 publications

References 37 publications

Preparation of SiO₂-Coated TiO₂Composite Materials with Enhanced Photocatalytic Activity Under UV Light

Preparation of SiO₂-Coated TiO₂Composite Materials with Enhanced Photocatalytic Activity Under UV Light

Superfícies fotocatalíticas de titânia em substratos cerâmicos: Parte I: Síntese, estrutura e fotoatividade

Synthesis variables effect on TiO2/polyester fabrics photoactivity and stability

Contact Info

Product

Resources

About

Photocatalytic activity of TiO2/SiO2 systems

Cited by 118 publications

References 37 publications

Preparation of SiO2-Coated TiO2Composite Materials with Enhanced Photocatalytic Activity Under UV Light

Preparation of SiO2-Coated TiO2Composite Materials with Enhanced Photocatalytic Activity Under UV Light

Superfícies fotocatalíticas de titânia em substratos cerâmicos: Parte I: Síntese, estrutura e fotoatividade

Synthesis variables effect on TiO2/polyester fabrics photoactivity and stability

Contact Info

Product

Resources

About

Preparation of SiO₂-Coated TiO₂Composite Materials with Enhanced Photocatalytic Activity Under UV Light

Preparation of SiO₂-Coated TiO₂Composite Materials with Enhanced Photocatalytic Activity Under UV Light