Pendulum and creep feed grinding of additively manufactured AISI 316L

Post-processing of additively manufactured metallic alloys – A review

“…Despite the importance of grinding as a finishing process, only a few research studies have been dedicated to grinding AM materials. Kirsch et al [143] recently published a paper on surface grinding of PBF-LB/316L stainless steel using conventional aluminium oxide wheels. The objective of this work was to investigate the differences in grindability when grinding conventional steel (cast, rolled, solution annealed, and water quenched) vs. two AM materials having different defect sizes and densities resulting from low and high VEDs (33.3 J/mm 3 Fig.…”

Pós-processamento de peças metálicas produzidas por manufatura aditiva

“…Em termos de retificação, Yazdanpanah et al (2021) relataram uma melhora da rugosidade de 14,75 µm (SLMed) para 0,25 µm R a . Usando retificação pendular, Blinn et al (2021) reduziram a rugosidade inicial (após L-PBF) de 10,99±1,27 µm S a para 1,98±0,95 µm S a e 128,65±15,47 µm S z para 17,14±4,15 µm S z em cerca de 3,6 s. Usando retificação pendular e profunda, a rugosidade inicial (após laser-SLM) foi reduzida de 42-44 µm para 6,0 µm e 2,5µm R z , respectivamente (KIRSCH et al, 2020). Durante a fase de revisão sistemática da literatura, apenas três artigos supracitados avaliaram o impacto da retificação nas características superficiais de amostras de aço 316L fabricadas por MA.…”