Pemetaan Nilai Suseptibilitas Magnetik Pasir Pantai Gandoriah Pariaman Sumatera Barat

Abstract

Mapping of magnetic susceptibility values of sand of Gandoriah beach, Pariaman West Sumatera has been carried out. The composition of sand beach was identified using X-Ray Fluorescence Spectroscopy (XRF) and the map of magnetic susceptibility and mass susceptibility of the sample were determined using Software Surfer 11. The samples were collected based on grid technique from 25 points location. The separation between magnetic particles and nan magnetic particles was done using iron sand separator for 1 time process.The result of the calculation of the magnetic degree of the sample using Iron Sand Separator for 1 time prosess showed that the values are in the range of 3,88 %-5,12 %. Magnetic and mass susceptibility values of the sample are in the range of (603,3-1351,46)×10-5 and (112,76–1086,85)×10-8 m3/Kg respectively. Magnetic and mass susceptibility of the concentrate (product of iron sand separator) are in the range of (1367,55–2155,9)×10-5 and (927,41–1774,28)×10-8 m3/Kg respectively. These values are in the range of Ilminate mineral that is (220-380000)×10-5 and (46-80000)×10-8 m3/Kg respectively. The percentage of Fe and Ti increases from 6,276 % to 54,549 % and from 0,441% to 5,102% respectively after being processed by iron sand separator. The results also showed that magnetic susceptibility values increase toward the sea water.

Penentuan Nilai Suseptibilitas Dan Ukuran Partikel Magnetik Pasir Alam Logas Kabupaten Kuantan Singingi Menggunakan Variasi Ukuran Ball Milling

“…Nilai suseptibilitas magnetik diperoleh berdasarkan nilai induksi magnetik solenoid tanpa inti (B 0 ) dan dengan inti (B T ) berupa pasir alam logas [5,6]. Grafik nilai suseptibilitas magnetik dari produk ball milling dua tahap sebagai fungsi waktu milling seperti pada Gambar 5.…”

Pengaruh Ukuran Bola Milling Terhadap Nilai Suseptibilitas Magnetik Dan Distribusi Ukuran Nanopartikel Magnetik Disintesis Dari Pasir Pantai Sungai Suci Bengkulu

“…Sintesis nanopartikel magnetik yang dilakukan oleh peneliti sebelumnya memiliki banyak jenis seperti metode sol gel, metode coprecipitation, metode hydrothermal, metode microwave danmetode ball milling. Metode ball milling kerap dipilih oleh banyak peneliti karena aplikasinya yang sederhana, efektif, ramah lingkungan dan hemat dari segi biaya [6,7]. Hasil sintesis nanopartikel magnetik yaitu produk BM2A, BM2B, BM2C diuji nilai induksi magnetiknya menggunakan probe pasco bertujuan untuk menentukan suseptibilitas magnetiknya.…”