Oxidation Behaviour of Microstructurally Highly Metastable Ag-La Alloy

Abstract

A new silver-based alloy with 2 wt.% of lanthanum (La) was studied as a potential candidate for electric contact material. The alloy was prepared by rapid solidification, performed by the melt spinning technique. Microstructural examination of the rapidly solidified ribbons revealed very fine grains of αAg and intermetallic Ag5La particles, which appear in the volume of the grains, as well as on the grain boundaries. Rapid solidification enabled high microstructural refinement and provided a suitable starting microstructure for the subsequent internal oxidation, resulting in fine submicron-sized La2O3 oxide nanoparticle formation throughout the volume of the silver matrix (αAg). The resulting nanostructured Ag-La2O3 microstructure was characterised by high-resolution FESEM and STEM, both equipped with EDX. High-temperature internal oxidation of the rapidly solidified ribbons essentially changed the microstructure. Mostly homogeneously dispersed nano-sized La2O3 were formed within the grains, as well as on the grain boundaries. Three mechanisms of internal oxidation were identified: (i) the oxidation of La from the solid solution; (ii) partial dissolution of finer Ag5La particles before the internal oxidation front and oxidation of La from the solid solution; and (iii) direct oxidation of coarser Ag5La intermetallic particles.

First-Principles and Experimental Study of Ge, V, Ta-Doped AgNi Electrical Contact Materials

“…Contacts are essential components in switching appliances, and their performance directly affects the reliable operation and service life of switching appliances. In the selection of low-voltage electrical contact materials, it is necessary to consider a variety of characteristics including physical properties, mechanical properties, electrical contact properties, thermal properties, chemical properties, processing and manufacturing properties, and so on [1,2]. Ag-based electrical contacts are employed in a multitude of light-and heavy-load electrical appliances due to their resistance to electrical abrasion, resistance to fusion welding, high electrical conductivity with very low contact resistance, and chemical stability [3][4][5].…”

Enhancement of Arc Erosion Resistance in AgCuO Electrical Contact Materials through Rare Earth Element Doping: First-Principles and Experimental Studies

“…Electrical contacts are essential components in a wide range of electrical and electronic equipment and play a critical role in ensuring the stability, reliability, and longevity of electrical systems [ 1 , 2 ]. However, during their service life, electrical contacts are subject to various physical and chemical erosion processes such as high temperatures, welding, wear, and arc discharge [ 3 , 4 , 5 ].…”