Origins of back stress strengthening in Fe-22Mn-0.6C (-3Al) TWIP steels

Zhi, Huihui; Antonov, Stoichko; Zhang, Cheng; Guo, Zihui; Su, Yanjing

doi:10.1016/j.msea.2020.139834

Cited by 20 publications

(1 citation statement)

References 29 publications

Supporting

Mentioning

Contrasting

Order By: Relevance

“…Where, j is the included angle between the external load and the normal of the slip plane (or the normal of the twin plane); l is the included angle between the external load and the slip direction (or twin direction) [21,22]. The Schmid factors of {111} < 110>slip system and {111} < 112>twin system for the texture orientation of rotating brass are calculated, which are 0.27 and 0.31, respectively.…”

Section: Texturementioning

confidence: 99%

Microstructure analysis and crack nucleation in TWIP steel tube at expansive deformation

Liu

Song

et al. 2021

Mater. Res. Express

View full text Add to dashboard Cite

The expansion test of twinning induced plastic (TWIP) steel tube was carried out at room temperature. Cracks appeared inside the tube edge when TWIP steel tube expands by 15.6%. The microstructure evolution, deformation mechanism and crack generation of TWIP steel after expansion were investigated by XDR OM TEM and EBSD. The results show that TWIP steel tube still austenite phase after expansion at room temperature; a great deal of dislocations are gathered around the grain boundaries and twin boundaries, the integral number of twins is high, and the mechanism of expansion deformation is the joint action of dislocations slip and deformation twins; Twins produce a large number of finer secondary or even multiple twins, intersecting each other; After expansion, the silk texture with direction of <111>∥X0 dominated by rotating brass texture {110}<111> is gradually produced through grain deformation and rotation; The proportion of small angle grain boundaries increased greatly; It is deduced that the criterion of crack nucleation is based on the difference between the dislocation pile-up energy (DPE) and the crack nucleation energy (CNE), and the expansion deformation process of TWIP steel satisfies the condition of crack nucleation.

show abstract

Section: Texturementioning

confidence: 99%