On the use of mini-CT specimens to define the Master Curve of unirradiated reactor pressure vessel steels with relatively high reference temperatures

Using mini-C(T) (4 mm thick, 0.16T) specimens to determine toughness in reactor pressure vessel steels permits the ductile to brittle transition temperature to be derived from small amounts of material and allows more effective use of surveillance specimens. However, questions have been raised as to whether the failure mechanisms are the same in miniature and large specimens, something that must be ensured when transferring fracture results obtained in mini-C(T) specimens to larger components. This work, performed within the FRACTESUS project, presents toughness measurements and detailed fractography on both a homogeneously brittle base metal and a relatively ductile, inhomogeneous weld to assess the transferability of fracture data. The fractography shows that brittle fracture initiates within the part of specimen experiencing small scale yielding, so long as the toughness measurement is valid. Similarly, although the precrack front asymmetry appears more marked in smaller specimens, as long as the deviation from planarity is within the ASTM E1921 limits, the asymmetry does not affect the location of the initiation site. For materials showing a variety of fracture modes, the fracture modes observed at the initiation sites are consistent with those observed in larger specimens. Where data are available, the stress and strain conditions at the initiation sites are also found to be consistent in mini-C(T) and larger specimens. These observations support the thesis that toughness measurements made on mini-C(T) specimens reflect the same material characteristics and failure mechanisms as those made on larger specimens.

show abstract

scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.

Contact Info

hi@scite.ai

10624 S. Eastern Ave., Ste. A-614

Henderson, NV 89052, USA

Blog Terms and Conditions API Terms Privacy Policy Contact Cookie Preferences Do Not Sell or Share My Personal Information

Made with 💙 for researchers

Part of the Research Solutions Family.

On the use of mini-CT specimens to define the Master Curve of unirradiated reactor pressure vessel steels with relatively high reference temperatures

Cited by 4 publications

References 17 publications

Mini-C(T) specimens for Master Curve analysis of structural steels operating within their ductile-to-brittle transition region

Mini-C(T) specimens for Master Curve analysis of structural steels operating within their ductile-to-brittle transition region

FRACTESUS Project overview: objectives, organisation and initial findings

Validity of Toughness Measurements From Miniature Specimens Failing in Different Fracture Modes

Contact Info

Product

Resources

About