“…The diagrams in Refs. [14][15][16] were consistent with the binary boundary constitutional diagrams just accepted from the literature, but meanwhile the Al-Cr and Al-Cu phase diagrams have been modified and new structures associated with several of their phases (see [17][18][19][20][21][22][23][24][25][26][27] and references therein).…”
Section: Introductionsupporting
confidence: 75%
“…At about 75 at.% Al an additional Al-Cr phase similar to lowtemperature Al 11 Mn 4 and forming in the solid-state was revealed [27]. Its formation was observed after a prolonged annealing at 650 • C and it was not destroyed by a short additional heating to 850 • C. According to our DTA the phase could transform slightly below 900 • C. On the other hand, the same as-cast samples annealed at 800 • C for 100 h contained only ␥ 2 and .…”
“…The diagrams in Refs. [14][15][16] were consistent with the binary boundary constitutional diagrams just accepted from the literature, but meanwhile the Al-Cr and Al-Cu phase diagrams have been modified and new structures associated with several of their phases (see [17][18][19][20][21][22][23][24][25][26][27] and references therein).…”
Section: Introductionsupporting
confidence: 75%
“…At about 75 at.% Al an additional Al-Cr phase similar to lowtemperature Al 11 Mn 4 and forming in the solid-state was revealed [27]. Its formation was observed after a prolonged annealing at 650 • C and it was not destroyed by a short additional heating to 850 • C. According to our DTA the phase could transform slightly below 900 • C. On the other hand, the same as-cast samples annealed at 800 • C for 100 h contained only ␥ 2 and .…”
“…Hexagonal Al 4 Cr isostructural to -Al 4 Mn has also been revealed in [7], confirmed in [5] and then in the more recent [8]. Also a base-centered orthorhombic structure with the lattice parameters essentially the same as -Al 4 Cr of [1] was revealed in [5], but associated in the latter with the higher-Al Al 5 Cr phase (also known in the literature as Al 11 Cr 2 or -phase).…”
“…The -phase revealed in Ref. [4] is formed by solid-state reaction ↔ + ␥ 2 . The temperature of the latter reaction has not yet been specified.…”
Section: Resultsmentioning
confidence: 98%
“…The Al-Cr binary phase diagram is accepted according to the recent updates included in Refs. [3][4][5]. For the convenience of the reader the relevant part of the updated Al-Cr phase diagram is reproduced in Fig.…”
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.