This is a PDF file of an unedited manuscript that has been accepted for publication. As a service to our customers we are providing this early version of the manuscript. The manuscript will undergo copyediting, typesetting, and review of the resulting galley proof before it is published in its final citable form. Please note that during the production process errors may be discovered which could affect the content, and all legal disclaimers that apply to the journal pertain.
AbstractExperiments were conducted to evaluate the flow properties of an Al-3Mg-0.2Sc alloy both without and with processing using equal-channel angular pressing (ECAP). The initial grain size was ~300 m and this was reduced to ~250 nm by ECAP and then increased to ~600 nm by annealing at 673 K for 10 min. Tests were conducted to determine the mechanical properties over seven orders of magnitude of strain rate from ~10 -4 to ~10 3 s -1 .The results confirm the validity of the Hall-Petch relationship in the material processed by ECAP. Shear banding occurred in the coarse-grained material during dynamic testing but in the ECAP-processed alloy there was only minor grain coarsening. There was evidence for dynamic strain ageing in both the coarse and the ultrafine-grained (UFG) alloy with a transition in flow mechanism at high temperatures from dislocation climb in the coarsegrained material to superplasticity in the UFG alloy.