“…After completely drying this solution at 100 °C, it was calcined at 500 °C for 2 h, and powdered to obtain WO 3 NPs. 49,51–53…”
Section: Methodsmentioning
confidence: 99%
“…After centrifuging the suspension, the solid material was dried for a day. Then, it was thoroughly washed with water and sintered at 250 °C for 5 h. 49,52–54…”
Section: Methodsmentioning
confidence: 99%
“…The binary AgI/WO 3 catalysts with varied AgI : WO 3 mole ratios were prepared by thoroughly hand-mixing aliquot amounts of each as-synthesized AgI and WO 3 semiconductors (at the expected mole ratio value) in an agate mortar for 20 min. 49…”
Section: Methodsmentioning
confidence: 99%
“…Comparing the values obtained with that of the corresponding blank MB solution ( A 0 ) gave C / C 0 (corresponding to A / A 0 based on the Beer–Lambert law) or degradation percentage of MB ( D % = ([ A − A 0 / A 0 ]) × 100 = ([ C − C 0 / C 0 ]) × 100). 49…”
Section: Methodsmentioning
confidence: 99%
“…The first part of the work focused on a brief characterization of the samples and kinetic study of the MB photodegradation. 49…”
The visible light-active AgI/WO3 binary photocatalyst has been characterized using XRD, FTIR spectroscopy, SEM-EDX, cyclic voltammetry (CV), photoluminescence (PL), and UV–vis DRS techniques.
“…After completely drying this solution at 100 °C, it was calcined at 500 °C for 2 h, and powdered to obtain WO 3 NPs. 49,51–53…”
Section: Methodsmentioning
confidence: 99%
“…After centrifuging the suspension, the solid material was dried for a day. Then, it was thoroughly washed with water and sintered at 250 °C for 5 h. 49,52–54…”
Section: Methodsmentioning
confidence: 99%
“…The binary AgI/WO 3 catalysts with varied AgI : WO 3 mole ratios were prepared by thoroughly hand-mixing aliquot amounts of each as-synthesized AgI and WO 3 semiconductors (at the expected mole ratio value) in an agate mortar for 20 min. 49…”
Section: Methodsmentioning
confidence: 99%
“…Comparing the values obtained with that of the corresponding blank MB solution ( A 0 ) gave C / C 0 (corresponding to A / A 0 based on the Beer–Lambert law) or degradation percentage of MB ( D % = ([ A − A 0 / A 0 ]) × 100 = ([ C − C 0 / C 0 ]) × 100). 49…”
Section: Methodsmentioning
confidence: 99%
“…The first part of the work focused on a brief characterization of the samples and kinetic study of the MB photodegradation. 49…”
The visible light-active AgI/WO3 binary photocatalyst has been characterized using XRD, FTIR spectroscopy, SEM-EDX, cyclic voltammetry (CV), photoluminescence (PL), and UV–vis DRS techniques.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.