Nano-mechanical behaviour of lithium metasilicate glass–ceramic

Fracture, roughness and phase transformation in CAD/CAM milling and subsequent surface treatments of lithium metasilicate/disilicate glass-ceramics

“…The pulverized surface in Fig. 8(a) emanated from surface and subsurface shear bands that were reported in our earlier investigation as the main deformation in nanoindentation of LMGC (Alao and Yin, 2015). Shear bands can form the plastic instability that localizes large shear strains in relatively thin bands during the material deformation process (Greer et al, 2013).…”

“…They can represent the material plastic deformation or serve as crack-initiating sites (Sergueeva et al, 2005). In milling, shear bands might have initiated microcracking through extensions of subsurface shear bands into underlying tensile matrices or from stress concentration sites at intersections of shear bands (Alao and Yin, 2015). Thus, the machining grooves in Fig.…”

Influência da cristalização na dureza, módulo de elasticidade e tenacidade à fratura por indentação em vitrocerâmicas de dissilicato de lítio (Li2 O.2SiO2 )

“…A dureza de contato, Hc, e o módulo de Young, E, foram medidos com carga de pico de 10 mN a uma taxa de aplicação de 0,1 a 2 mN/s com o objetivo de avaliar o efeito da taxa de aplicação da carga nas suas propriedades. A dureza de contato aumentou com a taxa de carregamento [19]. O efeito da alta pressão sobre o vidro dissilicato de lítio com composição estequiométrica Li 2 O.2SiO 2 no ambiente químico Si 2p, O 1s e Li 1s foi investigado por espectroscopia fotoelétrica de raios X. Foi verificado que a amostra cristalizada a 7,7 GPa indicou a formação de metassilicato de lítio e SiO 2 [20].…”