Multimode phonon structure of Be‐containing II ‐ VI mixed crystals determined by IR spectroscopic ellipsometry

Abstract

Spectroscopic ellipsometry in the infrared spectral range 250‐5000 cm‐1 is used for analysis of the dielectric response of Zn1‐x‐yBexMgySe and Zn1‐x‐yBexMnySe crystals grown by a high‐pressure Bridgman method. Ellipsometric spectra display features in the spectral range 390‐500 cm‐1 associated with BeSe‐type phonon modes. In the optical spectra of Zn1‐x‐yBexMgySe crystals both BeSe‐type and MgSe‐type lattice absorption bands are detected. The MgSe‐like modes are located at approximately 300 cm‐1. The complex dielectric functions can be reproduced using a model with two or three and one or two classical damped oscillators corresponding to the BeSe‐like and the MgSe‐like transverse‐optical phonon modes, respectively. The frequencies of longitudinal‐optical phonons have been derived from the dielectric loss functions. A red‐shift of the BeSe‐like phonons frequencies with a mean rate 0.42 cm‐1 (0.50 cm‐1) per mole percent of Mg (Mn) incorporated to the alloy has been found for examined concentration range x, y ≤ 0.25. A noticeable damping the intensities of BeSe‐type modes with increasing fraction of Mg and Mn dopant is observed in comparison to the strengths of BeSe‐type modes in Zn1‐xBexSe crystals. (© 2010 WILEY‐VCH Verlag GmbH & Co. KGaA, Weinheim)

Effects of Deposition Conditions of TiO2 Film and Substrate Prestrain on Film Void Geometries and Optical Properties in TiO2/PET Specimens

“…using variable‐angle spectroscopic ellipsometry. Wronkowska et al . used infrared spectroscopic ellipsometry to detect the multimode phonostructure of Be‐containing II–VI mixed crystals.…”