Multi-Scale Characterization by Neutronography and Electron Diffraction of Ni Coating on Cu-Ni-Al or Cast-Iron Glass Molds after Laser Cladding

Abstract

Laser cladding of a Ni based powder on Cu-Ni-Al or cast iron was performed with a 4kW continuous Nd: YAG laser. The Cu-Ni-Al and cast-iron substrates are used for their thermal properties in glass mold industry. But the issue of these materials is their lack of resistance on corrosion and abrasion. The role of the Ni based alloy is to protect the mold without affecting its thermal properties (Heat Affected Zone (HAZ)). The purpose of this research is to produce a well bonded Ni based melted powder without pores or cracks on a non-planar surface (curvilinear section). An investigation of the impact of the processing parameters, power (1500-3200 W), scanning speed (2.5-10 mm/s) and powder feeding rate (24.5-32.5 g/min) on the bonding quality, the porosity propagation and HAZ appearance is performed. The used methods are neutronography, Scanning Electron Microscopy, Energy Dispersive Spectroscopy and Electron BackScatter Diffraction (EBSD). These multi-scale techniques are obviously complementary. Neutronography is a well-adapted non-destructive method to observe the porosity in the volume thanks to the contrast between materials. EBSD analysis allows us to analyze the microstructural evolution of the coating notably by observing the dendrites growth. This same method also permits to observe the HAZ nature according to the laser cladding parameters. Those methods allowed to optimize the processing parameters in a way to obtain perfect bonding, to avoid porosity propagation and to limit the HAZ emergence.

Formation of a joint between deposited and base metals during laser cladding of a nickel-based powder onto a copper-based alloy

“…In the meantime, on the edges (according to the input laser power), less powder generates more power available for the interface fusion. According to the substrate composition, a high HAZ can be generated and induces a cracking behavior due to the high hardness as it was observed in previous researches conducted by the authors during laser cladding on cast iron [34].…”