Multi-passes warm rolling of AZ31 magnesium alloy, effect on evaluation of texture, microstructure, grain size and hardness

Abstract

Multi-passes warm rolling of AZ31 magnesium alloy, effect on evaluation of texture, microstructure, grain size and hardness Abstract. In this study the effect of multi-passes warm rolling of AZ31 magnesium alloy on texture, microstructure, grain size variation and hardness of as cast sample (A) and two rolled samples (B & C) taken from different locations of the as-cast ingot was investigated. The purpose was to enhance the formability of AZ31 alloy in order to help manufacturability. It was observed that multi-passes warm rolling (250°C to 350°C) of samples B & C with initial thickness 7.76mm and 7.73 mm was successfully achieved up to 85% reduction without any edge or surface cracks in ten steps with a total of 26 passes. The step numbers 1 to 4 consist of 5, 2, 11 and 3 passes respectively, the remaining steps 5 to 10 were single pass rolls. In each discrete step a fixed roll gap is used in a way that true strain per step increases very slowly from 0.0067 in the first step to 0.7118 in the 26th step. Both samples B & C showed very similar behavior after 26th pass and were successfully rolled up to 85% thickness reduction. However, during 10 th step (27 th pass) with a true strain value of 0.772 the sample B experienced very severe surface as well as edge cracks. Sample C was therefore not rolled for the 10th step and retained after 26 passes. Both samples were studied in terms of their basal texture, microstructure, grain size and hardness. Sample C showed an equiaxed grain structure after 85% total reduction. The equiaxed grain structure of sample C may be due to the effective involvement of dynamic recrystallization (DRX) which led to formation of these grains with relatively low misorientations with respect to the parent as cast grains. The sample B on the other hand showed a microstructure in which all the grains were elongated along the rolling direction (RD) after 90 % total reduction and DRX could not effectively play its role due to heavy strain and lack of plastic deformation systems. The microstructure of as cast sample showed a near-random texture (mrd 4.3), with average grain size of 44 µm & micro-hardness of 52 Hv. The grain size of sample B and C was 14µm and 27µm respectively and mrd intensity of basal texture was 5.34 and 5.46 respectively. The hardness of sample B and C came out to be 91 and 66 Hv respectively due to reduction in grain size and followed the well known Hall-Petch relationship.